The microstructures of B2-ordered NiA1 containing α-Fe precipitates have been investigated in terms of transmission electron microscopy. Fine precipitation of α-Fe (bcc structure) occurs in NiA1 by aging around 973K. The aging behavior was investigated by microhandness measurements and the temperature dependence of the yield strength of precipitate- comaining B2- ordered NiA1 was investigated by compression tests over the temperature range of 673-1273K. The fine precipitation of α-Fe was found to enhance greatly the low and intermediate temperature yield strength. When the deformation temperature is over 1073K, the strength of precipitate- containing NiA1 was comparable to ternary solid solution hardening NiA1-Fe. Dislocations bypass the particles during deformation and typical Orowan loops were observed surrounding the or-Fe particles after deformation.