通过金相显微镜、透射电镜、X射线仪以及力学性能测试等对自行设计的20MnSi钢的强韧化机制进行研究.结果表明试验钢性能取决于钢组织中原奥氏体晶粒的细化、弥散质点V(CN)的析出、珠光体片间距的减小和渗碳体片的变薄、以及珠光体数量的减少；此外,控轧控冷为20MnSi钢组织转变创造了热力学和动力学上的特殊条件,在铁素体基体上析出了细小且相互交错分布的针状铁素体,与平衡相铁素体相比较,它的形貌和结构特点对铁素体晶粒的塑性变形和微裂纹的扩展都会造成阻碍,因此,能够较好的改善钢的强韧性.
参考文献
| [1] | 王厚昕,李正邦.我国热轧钢筋的发展和现状[J].材料与冶金学报,2006(02):141-145. |
| [2] | 王信君.高强钢筋的研究及使用现状[J].四川建筑,2009(03):219-220. |
| [3] | 王学忠,刘佩明,穆国栋,路清祥,侯可强.HRB500钢筋的研制与生产分析[J].山东冶金,2005(03):20-22. |
| [4] | YI Hai-long,DU Lin-xiu,WANG Guo-dong,LIU Xiang-hua.Development of Nb-V-Ti Hot-Rolled High Strength Steel With Fine Ferrite and Precipitation Strengthening[J].钢铁研究学报（英文版）,2009(04):72-77. |
| [5] | 王瑞珍,杨忠民,车彦民,陈其安,马燕文,陈颖.低碳钢热轧钢筋再结晶控制轧制与控制冷却实现晶粒细化[J].钢铁,2004(02):47-50. |
| [6] | Emilio Bastidas-Arteaga;Philippe Bressolette;Alaa Chateauneuf;Mauricio Sanchez-Silva .Probabilistic Lifetime Assessment Of Rc Structures Under Coupled Corrosion-fatigue Deterioration Processes[J].Structural Safety,2009(1):84-96. |
| [7] | 翁宇庆.超细晶钢-钢的组织细化理论与控制技术[M].北京:冶金工业出版社,2003:34-36. |
| [8] | 陈伟,施哲,赵宇,庾郁梅.铌微合金化和控冷工艺开发HRB500抗震钢筋[J].材料热处理学报,2010(07):77-82. |
| [9] | Shim J H;Oh Y J .Ferrite nucleation potency of non-metallic inclusions in medium carbon steels[J].Acta Materialia,2011,49(12):2115-2122. |
| [10] | 梁冬梅,朱远志,周立新,方文胜.钢中针状铁素体及其非均匀形核机制[J].金属热处理,2011(12):105-111. |
| [11] | H. Landheer;S.E. Offerman;R.H. Petrov .The role of crystal misorientations during solid-state nucleation of ferrite in austenite[J].Acta materialia,2009(5):1486-1496. |
| [12] | M. Niikura;M. Fujioka;Y. Adachi;A. Matsukura;T. Yokota;Y. Shirota;Y. Hagiwara .New concepts for ultra refinement of grain size in super metal project[J].Journal of Materials Processing Technology,2001(3):341-346. |
| [13] | 刘刚,曲占元.针状铁素体钢的力学性能与显微结构[J].材料开发与应用,2010(01):6-8. |
| [14] | H. Beladi;G.L. Kelly;A. Shokouhi;P.D. Hodgson .The evolution of ultrafine ferrite formation through dynamic strain-induced transformation[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):343-352. |
| [15] | 谢建平.显微组织对针状铁素体型微合金化钢性能的影响[J].机电信息,2006(14):34-35. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%