The corrosion behavior of two different aged LY12 alloys in EXCO (234g/L NaCl, 50g/L KNO3,0. 1M HNO3) and MIL-H-600 (35g/L NaCl, 5g/L (NH4)2SO4) solutions were studied using electrochemical impedance spectroscopy (EIS) in conjunction with SEM technique respectively, and the pH variation of the above accelerated corrosion solution during materials corroding was also measured to characterize the corrosion processes. At the beginning of corrosion, EIS plots exhibited two capacitive arcs in the high frequency range (Ca) and mediate frequency range (Cy) originating from the original corroded surface and the newly formed interface respectively,and a low frequency inductive loop due to the relaxation phenomenon of reaction intermediates.In the EXCO.solution, the EIS results showed that once the exfoliation corrosion occurred, the inductive loop disappeared. The results also showed that the exfoliation corrosion susceptibility of state T6 is much higher than that of state T3, but the intergranular corrosion susceptibility has a reverse order. Based on the relationship of EIS results with SEM and metalloscopy morphologies of the corroding substrates and physic-chemical meaning of EIS parameters, an index (Cg/ Ca) has been proposed to characterize the extent of the localized corrosion, which variation tallies with the real corrosion extent correctly. Meanwhile, good agreement was found between the experimental results and the electrochemical model proposed and, good coherence between the electrochemical features and the distribution type of constituent particles of corroding material was observed.

参考文献

[1] M. J. Robinson;N. C. Jackson .Exfoliation corrosion of high strength Al-Cu-Mg alloys: effect of grain structure[J].British Corrosion Journal,1999(1):45-49.
[2] J de Damborenea;A Conde .[J].British Corrosion Journal,2000,35(01):48.
[3] A Conde;J de Damborenea .[J].Corrosion Science,1997,39(02):295.
[4] W H Colner;H R Francis .[J].Journal of the Electrochemical Society,1958,105(07):377.
[5] S M De Micheli;J R Galvele .[J].Corrosion Science,1970,10(06):795.
[6] 曹发和,程英亮,张昭,张鉴清,王建明,曹楚南.LC4铝合金在氯化钠溶液中的孔蚀特征[J].中国有色金属学报,2002(z1):245-249.
[7] F H Cao;Z Zhang;Y L Cheng;J Q Zhang,J F Li,J M Wang ,C N Cao .[J].Acta Metall Sinica(English Lett),2003,16(01):15.
[8] F.H.Cao,Z.Zhang,Y.L.Cheng,J.F.Li,J.Q.Zhang,C.N.Cao.ELECTROCHEMICAL FEATURES DURING PITTING CORROSION OF LY12 ALUMINUM ALLOY IN DIFFERENT NEUTRAL SOLUTIONS[J].金属学报(英文版),2003(04):319-326.
[9] D J Kelly;M J Robinson .[J].Corrosion,1993,49(10):787.
[10] M Habashi;E Bonte;J Galland .[J].Journal of Bodu,Corrosion Science,1993,35(04):168.
[11] D Li;S Z Zuo;B L Guo .[J].中国腐蚀与防护学报,1995,15(03):203.
[12] ASTM G34-79, Annual Book of ASTM Standards[M].ASTM,West Conshohocken,PA,1994:129.
[13] S E Frers;M M Stefenel;C E Mayer;J Chierchie .[J].Journal of Applied Electrochemistry,1990,20(06):996.
[14] J B Bessonz;D R Salinas;C E Mayer;M Ebert ,W J Lorenz .[J].Electrochimica Acta,1992,37(12):2283.
[15] C M A Brett .[J].Corrosion Science,1992,33(02):203.
[16] D D Macdonald;E Sikora;G Engelhardt .[J].Electrochimica Acta,1998,43(01):87.
[17] M Keddam;C Kuntz;H Takenouti;D Schuster ,D Zuili .[J].Electrochimica Acta,1997,42(01):87.
[18] D H Van der Weude;E P M Van Westing;H W de Wit .[J].Corrosion Science,1994,36(04):643.
[19] M Gao;C R Feng;R P Wei .[J].Metallurgical and Materials Transactions,1998,A 29:1145.
[20] A J Aldykewicz;H S Isaacs;A J Davenport .[J].Journal of the Electrochemical Society,1995,142(10):3342.
[21] P L Cabot;J A Garrido;E Perez;A H Moreira,P T A Sumodjo ,W Proud .[J].Electrochimica Acta,1995,40(04):447.
[22] E Brillas;P L Cabat;F Centellas;J A Garrido,E Perez ,R M Rodriguez .[J].Electrochimica Acta,1998,43(07):799.
[23] M H Shao;Y Fu;R G Hu;C J Lin .[J].Materials Science and Engineering A,2003,344:323.
[24] J D Bernardin;I Mudawar .[J].International Journal of Heat and Mass Transfer,1995,18(05):863.
[25] F. -H. Cao;Z. Zhang;J. -F. Li;Y. -L. Cheng;J. -Q. Zhang;C. -N. Cao .Exfoliation corrosion of aluminum alloy AA7075 examined by electrochemical impedance spectroscopy[J].Materials and Corrosion,2004(1):18-23.
[26] Q X Zha.Introduction of Electrode Process Kinetics[M].北京:语文出版社:1.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%