利用有限元分析软件MSC.Marc,研究板料初始温度、压边力、保压时间等工艺参数对制件厚度、回弹的影响规律,并通过6061铝合金板材热冲压实验验证仿真分析的可靠性.结果表明:板料热冲压初始温度在465～565℃范围内变化时对该制件厚度分布和回弹量的影响不大;压边力对制件成形质量影响明显,本工况下选用3kN较为合适;兼顾制件保压结束时刻的温度以及最终的回弹量,保压时间选择5s左右比较合适.进一步开展成形制件热处理后的力学性能测试分析,并与常规固溶淬火-时效热处理后的6061-T6铝合金进行比较,发现热冲压制件的力学性能并未弱化,且同一热冲压制件不同位置硬度差异在10％以内.
参考文献
| [1] | Daoming Li;Amit K. Ghosh.Biaxial warm forming behavior of aluminum sheet alloys[J].Journal of Materials Processing Technology,20043(3):281-293. |
| [2] | 王孟君;任杰;黄电源;姜海涛.汽车用5182铝合金板材的温拉伸流变行为[J].中国有色金属学报,2008(11):1958-1963. |
| [3] | Paolo F. Bariani;Stefania Bruschi;Andrea Ghiotti;Francesco Michieletto.Hot stamping of AA5083 aluminium alloy sheets[J].CIRP Annals,20131 CD/ROM(1 CD/ROM):251-254. |
| [4] | Mohamed S. Mohamed;Alistair D. Foster;Jianguo Lin;Daniel S. Balint;Trevor A. Dean.Investigation of deformation and failure features in hot stamping of AA6082: Experimentation and modelling[J].International Journal of Machine Tools & Manufacture: Design, research and application,20121(1):27-38. |
| [5] | 傅垒;王宝雨;孟庆磊;周靖;林建国.铝合金热冲压成形质量影响因素[J].中南大学学报（自然科学版）,2013(3):936-941. |
| [6] | 周靖;王宝雨;林建国;傅垒;马闻宇.铝合金车门防撞梁热冲压成形缺陷[J].中国有色金属学报（英文版）,2014(11):3611-3620. |
| [7] | 潘道召;王芝秀;李海;郑子樵.双级时效对6061铝合金拉伸性能和晶间腐蚀性能的影响[J].中国有色金属学报,2010(3):435-441. |
| [8] | 盈亮;戴明华;胡平;闫巧云.6061-T6铝合金高温本构模型及温成形数值模拟[J].中国有色金属学报,2015(7):1815-1821. |
| [9] | Vijay Soundararajan;Srdja Zekovic;Radovan Kovacevic.Thermo-mechanical model with adaptive boundary conditions for friction stir welding of Al 6061[J].International Journal of Machine Tools & Manufacture: Design, research and application,200514(14):1577-1587. |
| [10] | 赵俊;湛利华;史博.6061铝合金高温拉伸流变行为[J].塑性工程学报,2014(3):111-115. |
| [11] | 伍世棋;阳湘安.基于CAE的车身支撑板冲模设计[J].模具工业,2010(4):38-41. |
| [12] | 谭海艳 .汽车钢板弹簧热成形工艺的研究及仿真[D].武汉理工大学,2008. |
| [13] | 邓明;夏庆发;杜丽伟.基于变形区显微状态分析的精冲成形机理研究[J].塑性工程学报,2005(6):71-73. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%