采用柠檬酸络合-有机模板剂分解法制备了不同原子配比的La-Co-Ce-O混合氧化物催化剂. 这些样品具有较大的比表面积(》100 m2/g)和均匀的孔径(3.7～3.9 nm), 并显示出较高的热稳定性. 模板剂分解法制备的样品中CeO2和Co3O4的分散性以及对CO和丙烷氧化的催化活性均明显优于传统共沉淀法制备的样品. 催化剂活性并不与表面钴原子分数成正比,而与表面钴、铈物种间的协同效应密切相关,当表面钴、铈原子分数接近时,协同效应最佳,催化氧化性能最好.
参考文献
| [1] | Summers J C;Sawyer J E;Frost A C .[J].ACS Symposium Series,1992,495:98. |
| [2] | 邹志强,孟明,查宇清,谢亚宁,胡天斗,刘涛.介孔混合氧化物催化剂La-Co-Zr-O的制备与表征[J].催化学报,2006(02):129-134. |
| [3] | Ahn W-S;Kim N-K;Jeong S-Y .[J].Catalysis Today,2001,68(1-3):83. |
| [4] | Chen LY.;Jaenicke S.;Chuah GK. .Propylene epoxidation with hydrogen peroxide catalyzed by molecular sieves containing framework titanium[J].Journal of molecular catalysis, A. Chemical,1998(2/3):281-292. |
| [5] | Chaudhari K;Bal R;Srinivas D;Chandwadkar A J Sivasanker S .[J].Microporous and Mesoporous Materials,2001,50(2-3):209. |
| [6] | Sing K S W;Everett D H;Haul R A W;Moscou L Pierotti R A Rouquerol J Siemieniewska T .[J].Pure and Applied Chemistry,1985,57(04):603. |
| [7] | Kang M;Song M W;Lee C H .[J].Applied Catalysis A:General,2003,251(01):143. |
| [8] | Harrison P G;Ball I K;Daniell W;Lukinskas P Cspedes M Miró E E Ulla M A .[J].CHEMICAL ENGINEERING JOURNAL,2003,95(1-3):47. |
| [9] | Meng M;Zha Y Q;Luo J Y;Hu T D Xie Y N Liu T Zhang J .[J].Applied Catalysis A:General,2006,301(02):145. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%