采用普通对称式方法(不施加复合能场)和非对称下沉式方法(施加超声波/电磁复合能场)对1060铝合金板带坯进行铸轧试验；研究了复合能场对铝合金板带组织和性能的影响.结果表明:施加复合能场后,铸轧速度(1.2～1.4 m.min-1)提高了30％,铝合金板带的组织由粗大的柱状晶转变为均匀细小的等轴晶,其抗拉强度、屈服强度、伸长率和硬度分别提高了25.03％,24.37％,40.09％和10.95％.
参考文献
| [1] | 王东,马宗义.轧制工艺对7050铝合金显微组织和力学性能的影响[J].金属学报,2008(01):49-54. |
| [2] | 王祝堂.低碳铝工业：新时代的要求[J].世界有色金属,2010(05):20-23. |
| [3] | Eskin GI.;Eskin DG. .Production of natural and synthesized aluminum-based composite materials with the aid of ultrasonic (cavitation) treatment of the melt[J].Ultrasonics sonochemistry,2003(4/5):297-301. |
| [4] | S.Kamado;T.Kosaka .Fabrication of 5052 aluminum alloy thin slab by electromagnetic casting and mechanical properties of its cold- rolled sheet[J].Materials Science Forum,2000(0):473-478. |
| [5] | 毛大恒.铝及铝合金电磁连铸轧新技术--电磁场对金属凝固的作用机理[J].矿冶工程,1996(02):68. |
| [6] | 聂朝辉,毛大恒,张云芳.超声波处理对铸轧铝板带组织的影响[J].轻合金加工技术,2006(04):10-13. |
| [7] | MAO Da-heng,ZHANG Yun-fang,NIE Zhao-hui,LIU Qiao-hong,ZHONG Jue.Effects of ultrasonic treatment on structure of roll casting aluminum strip[J].中南工业大学学报(英文版),2007(03):363-369. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%