在酸性环境下,屈服失效准则已不适用,环境断裂是主要的失效模式.因此,有针对性地改变油套管的设计和选材,将能够减少或防止油套管失效事故的发生.在满足屈服准则设计的基础上,对T95抗硫套管和C110准抗硫套管进行断裂力学设计,根据NACE D法试验计算出材料的临界应力强度因子KISSC,利用失效评估图(FAD)求出在不同条件下的T95和C110抗内压断裂强度.计算结果表明C110的抗内压断裂强度都要低于T95,对己下入C110套管的井,防止后期作业诱发裂纹至关重要.因此,酸性油气田油套管设计在满足屈服设计准则时,也要满足断裂力学设计准则,这一新的断裂力学设计方法为酸性油气田油套管设计和选材提供了重要参考价值.
参考文献
| [1] | Bruce E.High strength sour service C110 casing[A].SPE 52843[C].Amsterdam.1999:14. |
| [2] | Cermocky E P,David L.The qualification of C110-high strevIgth senr service casing-A statistical approach to evaluating material data across a single production heat lot[A].SPE 97579[C].Texas,2005:4. |
| [3] | Cernocky E P,Aaron V D,Paslay P R.Combined axial tension/compression and internal pressure testing of minipipe specimens in H2S environment to determine three dimensional(triaxial)stress states which produce crack initiation failure:explanation of the Dew test fixture,mini-pipe specimen,and preliminary test results[A].SPE 97577[C].Texas,2005,10. |
| [4] | Cermocky E P,Grimes W D.Recommended use of three separate stress formulas for the design of low alloy carbon steel production casing for sour HPHT wells[A].SPE 97572[C].Texas,2005:20. |
| [5] | API Bulletin 5C3-1994,Bulletin on formulas and calculations for casing,tubing,drill pipe and line properties[S],1994. |
| [6] | NACE TM0177-2005,Standard test method laboratory testing of metals for resistance to sulfide stress cracking and stress corrosion cracking in H2S environments[S],2005. |
| [7] | ISO11960:2004,Petroleum and natural gas industries-Steel pipes for use as casing or tubing for wells[S],2004. |
| [8] | 褚武扬.断裂与环境断裂[M].北京:科学出版社,2000:120. |
| [9] | ISO/TR 10400:2007,Petroleum and natural gas industries-Formula and calculation for casing,tubing,drill pipe and line pipe properties[S],2007. |
| [10] | Kermani M B,Turconi G L.Materials optimization in hydrocarbon production[A].NACE 2005[C].Texas,2005:111. |
| [11] | Janssen M,Zuidema J,Wnhill R J H.Fracture Mechanics[M].London:Spon Press,2004:165. |
| [12] | 李天雷.油井管硫化物应力开裂双悬臂梁法试验研究[D].成都:西南石油大学,2007:6. |
| [13] | Moore P W,Maldonado J G.Review of the recent API PRAC project attempt to evaluate the ISO DIS 10400 failure assessment diagram through full scale testing of pipe containing surface imperfections[A].SPE 97578[C].Texas,2005:16. |
| [14] | Julio G.Evaluation of the accuracy of the ISO DIS 10400 failure assessment diagram through full scale testing of pipe containing surface imperfections[A].API PRAC[C].Texas,2002:100300. |
| [15] | 孙永兴.油套管抗内压抗挤强度研究[D].成都:西南石油大学,2008:6. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%