采用高温包套轧制方法在普通轧钢轧机上首次成功的轧制出厚度为2.6 mm的高铌钛铝基合金板材.合金在轧制中的总变形量达到70%.板材表面质量良好,显微组织观察表明合金在轧制中发生了再结晶,但是变形后的组织并没有由于再结晶而明显细化.这主要是由于合金在轧制回炉保温和轧后随炉冷却过程中,长时间停留在高温区间,导致了合金晶粒的长大.
参考文献
| [1] | Kim Y W.Gamma Titanium Aluminides[C].Warrendale:TMS,1995:637. |
| [2] | Chen G L;Zhang W;Wang Y.Structural Intermetall-ics[C].New York:TMS,1993:319. |
| [3] | Chen G L;Zhang L C;Zhang W J .[J].INTERMETALLICS,1999,7(11):1211. |
| [4] | Liu Z C;Lin J P;Li S J et al.[J].Intermetallics,2002,10(07):65. |
| [5] | 鲁世强,黄伯云,贺跃辉,唐建成,张俊红.TiAl基合金的超塑性变形机理[J].稀有金属材料与工程,2003(07):481-485. |
| [6] | Semiatin S L;Vollmer D C;El-soudani S;Su C .[J].Scripta Metallurgica et Materialia,1990,24(08):1409. |
| [7] | Semiatin S L;Seetharaman V .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1995,26A:1073. |
| [8] | Clemens H Z .[J].Zeitschrift fur Metallkunde,1995,86(12):814. |
| [9] | Jewett T;Dahms M .[J].Journal of Materials Synthesis and Processing,1995,35:339. |
| [10] | 张俊红;黄伯云;周科朝.[J].Nonferrous Metals,2001:1055. |
| [11] | Koeppe C;Bartels A;Clemens H et al.[J].Materials Science and Engineering,1995,A201:182. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%