研究了钢板热浸镀55A1-Zn-1.5Si合金层的工艺,分析了不同的助镀剂配方及浸镀参数对镀层质量的影响,确定出了较理想的热浸镀工艺.结果表明:助镀剂基本不影响镀层的厚度,但助镀剂的选择对铝锌合金镀层耐蚀性能有直接影响;适用于钢板热漫镀55A1-Zn-1.5Si合金层的水溶性助镀剂配方为27%ZnCl2+lO%NH4C1;较理想的浸镀温度为640～660℃,浸镀时间为6min,提升速度为5 m·min-1.
参考文献
| [1] | Rocco AM.;Nogueira TMC.;Simao RA.;Lima WC. .Evaluation of chromate passivation and chromate conversion coating on 55% Al-Zn coated steel[J].Surface & Coatings Technology,2004(2/3):135-144. |
| [2] | Dominic Phelan;Bao Jiang Xu;Rian Dippenaar .Formation of intermetallic phases on 55 wt.%Al-Zn-Si hot dip strip[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2006(1/2):144-149. |
| [3] | F. Garcia;A. Salinas;E. Nava .The role of Si and Ti additions on the formation of the alloy layer at the interface of hot-dip Al-Zn coatings on steel strips[J].Materials Letters,2006(6):775-778. |
| [4] | 李华飞,郑家燊,俞敦义.添加稀土对55%Al-Zn镀层的影响[J].华中科技大学学报(自然科学版),2003(05):107-109. |
| [5] | 刘军.热浸镀55%铝锌合金镀层助镀剂的选择[J].机械工程材料,2003(12):42-43. |
| [6] | 文九巴,李全安,赵万祥,王志辉.富Ce混合稀土铝合金热浸镀渗工艺研究[J].热加工工艺,2003(04):13-14. |
| [7] | 邹友忠,倪志坚,曹关中,王继龙.A3钢热浸镀55%Al-Zn合金工艺及涂层性能研究[J].材料保护,2001(07):31-33. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%