2Y-PSZ/TRIP steel composites have been sintered by hot-pressing method. Their microstructure and mechanical properties were investigated by means of SEM, TEM, XRD and static tension, split Hopkinson pressure bar method.The results showed that the strength and elastic modulus of 2Y-PSZ/TRIP steel composites at room temperature decreased with the increase of 2Y-PSZ content. The main reason was that the combining strength was quite weak between the grains of ZrO2. Distortion induced martensite transformation and plasticity during the dynamic loading increased the strength and distortion capability of the composites. The transformation was carried out mainly through twins formation. The shape of martensite induced by distortion was lamellate with substructures of twins. The habit plane was near {259}γ with no mid-ridge and no explosion phenomena. The interface was straight between the austenite and martensite induced by distortion. The increase of 2Y-PSZ content, on the one hand, made the composite dynamic flow stress improved. Thereby, the fracture strength was improved. On the other hand, it depressed both the distortion capability and the martensite transformation induced by distortion. This resulted in the decrease of dynamic fracture strength.
参考文献
| [1] | F D Fischer;G Reisner;E Werner;K Tanaka, G Cailletaud and T Antretter .[J].International Journal of Plasticity,2000,16:723. |
| [2] | Yeon-Dil Jung;Sung-Churl Choi;Chang-Seob Oh .[J].Journal of Materials Science,1997,32:3841. |
| [3] | Yu ZHOU.[A].Harbin,1996:35-50. |
| [4] | Y. G. Jung;U. Palk .Influence of the particle size and phase type of zirconia on the fabriacation and residual stress of zirconia/stainless-steel 304 functionally gradient material[J].Journal of Materials Science,1999(21):5407-5416. |
| [5] | Zhiguang LI;Minoru Taya;Martin I Dunn.[J].Journal of the American Ceramic Society,1995:1633. |
| [6] | T Y Hus.Martensite and Martensitic Phase Transformation[M].北京:科学出版社,1999:693. |
| [7] | Kaiming LIANG;Koufen GU;G Fantozzi .[J].J Chinese Ceram Soc,1994,22(01):29. |
| [8] | Yonglin KANG;Bo WANG .[J].Journal of Iron and Steel Research,1999,11(03):62. |
| [9] | 赵密,郭英奎,俞泽民,宁志良,王君祥.烧结温度对不锈钢（316L）致密性及强度的影响[J].哈尔滨理工大学学报,2000(03):105-107. |
| [10] | Dongbo LI .[D].Harbin Institute of Technology,1999. |
| [11] | Reisong GUO;Shu CAI;Huiming JI;Houzheng WU.Structural Ceramic in Engineering[M].天津:天津大学出版社,2002:172. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%