以石油焦为原料,研究了原料粒度及混入中温沥青、酚醛树脂、田菁粉和淀粉等添加荆对管式炭膜孔结构和膜强度的影响.结果表明,随原料平均粒径的减小,所制得管式炭膜的平均孔径减小,但强度增大;加入酚醛树脂、田菁粉和淀粉等添加剂使炭膜孔径增大,但强度减小,而加入中温沥青则与之相反;以田菁粉为添加剂时炭膜的平均孔径达0.319μm,强度为4.40N/mm,以中温沥青为添加剂时炭膜的平均孔径为0.174μm,但强度高达13.78N/mm.
The influence on the pore structure and strength of the tube carbon membrane by changing the size of raw materials granularity and mixing with medium temperature pitch, phenolic resin, sesbania powder, starch as additives is investigated. The results show that the average pore size of tube carbon membrane decreases with the decrease of the average particle size of raw materials, but the strength grows. And the pore size of carbon membrane increase largely when phenolic resin, sesbania powder, starch are added, but the strength decreased, while the temperature pitch is in the opposite. To sesbania powder as additive, the average pore size is up to 0. 319μm, its strength is 4. 40N/mm. To medium temperature pitch as additive, the average pore size is 0. 174μm, but its strength is up to 13. 78N/mm.
参考文献
| [1] | 王同华;刘淑琴;尤隆渤 et al.煤基管状炭膜支撑体的研究[J].煤炭转化,1998,21(03):73. |
| [2] | Wei Wei;Hu Haoquan;You Longbo et al.Preparation of carbon molecular sieve membrane form phenol-formaldehyde novolac resin[J].Carbon,2002,40(03):465. |
| [3] | 王同华,魏微,刘淑琴,尤隆渤,蔡天锡.管状多孔炭膜的研究[J].新型炭材料,2000(01):6-11. |
| [4] | Damle A S;Gangwal S K;Venkataraman V K .Carbon membranes for gas separation:Developmental studies[J].Gas Separation and Purification,1994,8(03):137. |
| [5] | 王树森;曾美云;王志忠 .分子筛炭膜的形态结构研究[J].北京工业大学学报,1995,21(04):90. |
| [6] | 魏微;秦国彤;候胜德.炭膜及其在环境领域中的应用[J].Techniques Equipment Environmental Pollution |
| [7] | 王振余;郭树材 .炭膜处理染料水溶液的研究[J].膜科学与技术,1997,17(05):7. |
| [8] | 张永刚,卢明超.管式炭膜制备工艺对膜孔结构的影响[J].功能材料,2009(08):1365-1367,1371. |
| [9] | 卢明超,张永刚.炭膜制备及其孔结构调控[J].材料导报,2007(03):101-103,107. |
| [10] | 魏芸,李忠全.气泡法测量多孔材料孔径的简化解析法[J].粉末冶金工业,2004(06):20-23. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%