研究合金元素Bi对AM60镁合金显微组织和力学性能的影响.借助金相显微镜(OM)、扫描电镜(SEM)和X射线衍射(XRD)对添加Bi的AM60镁合金观察与分析.结果表明:Bi的添加细化了合金显微组织,提高合金力学性能；当Bi的质量分数为1.0％,合金的抗拉强度、硬度和伸长率由176.3 MPa,54.5HBS,7.38％提高至200.2 MPa,70.5HBS和9.68％,分别提高13.6％,29.4％,31.2％.进一步提高Bi加入量,合金显微组织变粗大,性能下降.
参考文献
| [1] | A. A. Luo .Recent magnesium alloy development for elevated temperature applications[J].International Materials Reviews,2004(1):13-30. |
| [2] | Cole G S .Issues that influence magnesium' s use in the automotive industry[J].Materials Science Forum,2003,419/422(01):43-50. |
| [3] | Govind;Nair K S;Mittal M C et al.Development of rapidly solidified(RS) magnesium-alumininm-zinc alloy[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2003,359(1/2):150-157. |
| [4] | Flemings M C .Behavior of metal alloys in the semi-solid state[J].Metallurgical and Materials Transactions,1991,22(05):957-981. |
| [5] | 袁广银,孙扬善,王震.Sb低合金化对Mg-9Al基合金显微组织和力学性能的影响[J].中国有色金属学报,1999(04):779-784. |
| [6] | 黄正华,郭学锋,张忠明.Ce对AZ91D镁合金力学性能与阻尼性能的影响[J].稀有金属材料与工程,2005(03):375-379. |
| [7] | 陈刚,彭晓东,范培耕,谢卫东,魏群义,马宏,杨艳.Sr和Y对AZ31镁合金组织与耐蚀性能的影响[J].中国有色金属学报（英文版）,2011(04):725-731. |
| [8] | 戴永年.二元合金相图集[M].北京:科学出版社,2009:217. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%