通过激光熔化沉积TA15+30%TiC(体积分数)混合粉末,在TA15钛合金表面制备出钛基复合材料涂层,分析了涂层的组织、硬度及界面结合强度.结果表明,激光熔化沉积过程中原始TiC颗粒发生溶解,并在凝固过程中重新析出细小的TiC,TiC有等轴状及枝晶两种形态,涂层中存在部分未熔的TiC颗粒;涂层硬度达HRC 60;涂层与基体界面为完全冶金结合,涂层的界面结合强度大于310MPa,抗剪切强度为330MPa;经弯曲及热震试验后,涂层未出现剥落现象,表明涂层与基体具有很好的相容性.
参考文献
| [1] | 周慧,刘正堂,李争显,杜继红.钛合金表面微弧氧化膜及抗氧化性能的研究[J].稀有金属材料与工程,2005(11):1835-1838. |
| [2] | Bacci T et al.[J].Materials Science and Engineering A,2000,283(01):189. |
| [3] | Zhecheva A;Sha W;Malinov S;Long A .Enhancing the microstructure and properties of titanium alloys through nitriding and other surface engineering methods[J].Surface & Coatings Technology,2005(7):2192-2207. |
| [4] | Vadiraj A et al.[J].Materials Science and Engineering A,2007,445-446:446. |
| [5] | 王文波,徐重,贺志勇,王振霞,张平则.双辉技术渗铌对Ti-6Al-4V合金氧化性能的影响[J].稀有金属材料与工程,2007(05):869-873. |
| [6] | Mridha S;Baker T N .[J].Journal of Materials Processing Technology,1997,63(1-3):432. |
| [7] | Sun RL.;Guo LX.;Dong SL.;Yang DZ. .Laser cladding of Ti-6Al-4V alloy with TiC and TiC plus NiCrBSi powders[J].Surface & Coatings Technology,2001(2/3):307-312. |
| [8] | Sun RL.;Mao JF.;Yang DZ. .Microstructural characterization of NiCr1BSiC laser clad layer on titanium alloy substrate[J].Surface & Coatings Technology,2002(2/3):199-204. |
| [9] | Xue Y;Wang HM .Microstructure and wear properties of laser clad TiCo/Ti2CO intermetallic coatings on titanium alloy[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2005(1/4):278-286. |
| [10] | Jian LN;Wang HM .Microstructure and wear behaviours of laser-clad Cr13Ni5Si2-based metal-silicide coatings on a titanium alloy[J].Surface & Coatings Technology,2005(2/3):305-310. |
| [11] | Wang Y;Wang H M .[J].Applied Surface Science,2004,229(1-4):81. |
| [12] | J. A. Vreeling;V. Ocelik .Ti-6Al-4V strengthened by laser melt injection of WC_p particles[J].Acta materialia,2002(19):4913-4924. |
| [13] | H.C. Man;S. Zhang;F.T. Cheng .MICROSTRUCTURE AND FORMATION MECHANISM OF IN SITU SYNTHESIZED TiC/Ti SURFACE MMC ON Ti-6Al-4V BY LASER CLADDING[J].Scripta materialia,2001(12):2801-2807. |
| [14] | 于翔天,王华明.激光熔化沉积（TiB+TiC）/TA15原位钛基复合材料的显微组织与力学性能[J].复合材料学报,2008(04):113-118. |
| [15] | 席明哲,虞钢,张永忠,石力开.同轴送粉激光成形中粉末与激光的相互作用[J].中国激光,2005(04):562-566. |
| [16] | Zhang Yongzhong et al.[J].Journal of Materials Processing Technology,2008,206(1-3):438. |
| [17] | Cai Lifang et al.[J].Journal of University of Science and Technology Beijing,2006,13(06):551. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%