The behavior of gaseous nitriding on the surface nanocrystallized (SNCed) steel was investigated. The mild steel discs were SNCed on one side by using the method of ultrasonic shot peening. The opposite side of the discs maintained the original coarse-grained condition. The gaseous nitriding was subsequently carried out at three different temperatures:460, 500 and 560℃. The compound layer growth and diffusion behavior were then studied. It was revealed that SNC pretreatment greatly enhances both diffusion coefficient D and surface reaction rate. As a result, nitriding time could be reduced to the half. It was also found that the growth of compound layer with nitriding time conformed with parabolic relationship from the start of nitriding process in the SNCed samples.
参考文献
| [1] | N.R. Tao;M.L. Sui .Surface nano crystallization of iron induced by ultrasonic shot peening[J].Nanostructured Materials,1999(4):433-440. |
| [2] | G. Liu;J. Lu;K. Lu .Surface nanocrystallization of 316L stainless steel induced by ultrasonic shot peening[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2000(1):91-95. |
| [3] | Ke Lu;Jian LU J .[J].Materials Science and Technology,1999,15:193. |
| [4] | Feng Gan .Investigation on the surface nanocrystallization treatment to a low carbon steel and its nitriding process[D].Master Dissertation. Nanjing University of Science and Technology,1999. |
| [5] | M J Hu;J S Pan.[A].:71. |
| [6] | Kazuo Fueki .[J].Bulletin of the Japanese Institute of Metals,1975(14):2,125. |
| [7] | M McLean;E D Hondros.[J].Journal of Materials Science,1973(08):349. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%