目的：探究超声波功率对镀层耐腐蚀性的影响规律。方法将超声波功率分为50,70,90,110 W4个等级,利用湿法超声机械镀锌设备制备4种镀层。用多功能扫描电子显微镜观察镀锌层的微观表面形貌,并分析镀锌层厚度,测试镀锌层的耐腐蚀性能以及镀层与基体的附着强度。结果功率为50 W时获得的镀层厚度最大,表面质量、耐腐蚀性能最差；功率为110 W时获得镀层表面质量、耐腐蚀性能最好。结论随功率的增大,镀层表面质量明显提高,镀层耐腐蚀性有逐渐增加的趋势。
ABSTRACT:Objective To explore the influencing law of the ultrasonic power on the corrosion resistance of the coating. Methods Under the four levels of ultrasonic power(50, 70, 90, 110 W),four kinds of mechanical zinc-coatings were prepared by Wet ultra-sound mechanical galvanizing equipment. The surface topography of the coatings was observed and studied by SEM. The coatings thickness was measured, the corrosion resistance was determined and the bonding strength between the coating and the substrate was studied. Results When the ultrasonic power was 50 W, the corrosion resistance and surface quality of the zinc-coating were worse than those of others. While the corrosion resistance and surface quality of the zinc-coating were the best when the ultrasonic power was 110 W. Conclusion The surface quality of the coating was significantly improved and the corrosion resistance of the coating showed an increasing trend with increasing power.
参考文献
| [1] | 陈菡.镀锌防腐工艺[J].钢铁,2007(07):38-42. |
| [2] | 徐明玉,牛宗伟,李明哲.湿法超声机械镀锌-铝层的性能研究[J].电镀与涂饰,2014(09):366-368. |
| [3] | 李广敏,牛宗伟,董海青.湿法超声机械镀锌技术研究[J].表面技术,2014(01):63-66. |
| [4] | 王胜民,何明奕,刘丽,赵晓军,谭蓉.机械镀锌沉积机理的研究[J].材料科学与工艺,2008(04):535-538. |
| [5] | 卢杰,石岩.机械镀锌层微观形貌及有机硅表面封孔耐腐蚀处理[J].表面技术,2007(06):36-38. |
| [6] | 卢杰.不同粒度金属粉形成机械镀层形貌及耐腐蚀性能研究[J].表面技术,2008(05):41-44. |
| [7] | 王胜民,赵晓军,何明奕,刘丽,裴和中,谭蓉.锌粉颗粒形状对机械镀锌层性能的影响[J].材料工程,2009(11):84-87. |
| [8] | 赵增典,陈磊,李德刚,黄保雷.机械镀镀层与金属粉末相关性的研究[J].材料保护,2008(08):64-66. |
| [9] | 王胜民,何明奕,赵晓军,刘丽,谭蓉.机械镀Zn-RE复合镀层的结构[J].材料热处理学报,2010(01):137-141. |
| [10] | 何明奕;刘丽;王胜民.机械镀锌原理及应用[M].北京:机械工业出版社,2003 |
| [11] | 王兆华,杨瑞嵩,张鹏,刘元洪.机械镀锌成膜机理探讨[J].材料保护,2013(08):52-55. |
| [12] | 李广敏,牛宗伟.基于超声振动的机械镀锌工艺[J].电镀与涂饰,2014(01):21-23. |
| [13] | 山东理工大学 .湿法超声机械镀装置[P].中国,103205745,2013-07-17. |
| [14] | Komarov SV;Son SH;Hayashi N;Kaloshkin SD;Abramov OV;Kasai E .Development of a novel method for mechanical plating using ultrasonic vibrations[J].Surface & Coatings Technology,2007(16/17):6999-7006. |
| [15] | S. Romankov;S.V. Komarov;E. Vdovichenko .Fabrication of TiN coatings using mechanical milling techniques[J].International Journal of Refractory Metals & Hard Materials,2009(2):492-497. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%