本研究用一种操作简单、适合规模化、低成本的方法制备六方氮化硼粉末.研究了硼、氮元素的物质的量比值,烧成制度,助熔剂的添加量对产物物相成份和颗粒形貌的影响,并对酸洗和碱洗对产物中杂质的去除效果进行了比较.用X-射线衍射仪(XRD)、扫描电镜(SEM)对制备的产物样品进行了分析表征,发现用该工艺制得的六方氮化硼纯度可达95.6%,去杂后纯度可达99%以上,晶粒直径约为0.2～0.5 μm,厚度在60～70 nm,晶粒尺寸比较均匀.
参考文献
| [1] | 胡婉莹.连续合成六方氮化硼的新工艺[J].现代技术陶瓷,2002(02):35-36,47. |
| [2] | 郑盛智,刁杰.六方氮化硼的合成与高温精制[J].辽东学院学报（自然科学版）,2008(02):69-70,84. |
| [3] | Baraton M I;Boulanger L;Cauchetier M .Nanometric boron nitride powders:laser synthesis,characterization and FT-IR surface study[J].Journal of the European Ceramic Society,1994,13:371-378. |
| [4] | X. P. Hao;D. L. Cui;G. X. Shi .Low temperature benzene thermal synthesis and characterization of boron nitride nanocrystals[J].Materials Letters,2001(6):509-513. |
| [5] | Sun C H;Guo C L;Ma X J .A facile route to prepare boron nitride hollow particles at 450 ℃[J].Journal of Crystal Growth,2009,311:3682-3686. |
| [6] | Liang-xu Lin;Ying Zheng;Zhao-hui Li .A simple method to synthesize polyhedral hexagonal boron nitride nanofibers[J].Solid state sciences,2007(12):1099-1104. |
| [7] | 葛雷,杨建,丘泰.六方氮化硼的制备方法研究进展[J].电子元件与材料,2008(06):22-25,29. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%