采用真空烧结法制备90W-7Ni-3Fe 高密度钨合金,通过材料试验机、SEM、XRD 等表征了材料的性能与显微结构.结果表明:钨合金的相对密度、强度、塑性均随烧结温度升高先上升后下降,1440℃烧结试样的性能最佳,其相对密度、抗弯强度、抗拉强度、伸长率和断面收缩率分别为99.2%、1920.5 MPa、1086.7 MPa、22.8%和24.4%.钨合金单纯由体心立方的钨相和面心立方的Fe3Ni2固溶体相组成,未出现其他杂质相.在1360~1460℃的烧结温度范围内,随温度的升高,钨合金断裂形态依次发生以下转变:沿晶脆性断裂、穿晶脆性断裂、韧窝韧性断裂、粘接相撕裂韧性断裂和穿晶脆性断裂.
@@@@90W-7Ni-3Fe high-density tungsten alloys were fabricated by vacuum sintering method. Material testing machine, SEM and XRD were adopted to characterize the performance and microstructure of the alloys. The results show that the relative density, strength and plasticity of tungsten alloys increase at first and decrease afterwards with the increase of the sintering temperature. The sample sintered at 1 440℃demonstrates the optimal performance. Its relative density, bending strength, tensile strength, elongation and cross section shrinkage ratio are 99.2%, 1 920 MPa, 886 MPa, 22.83%and 24.37%, respectively. The tungsten alloy is simply made up of body centered cubic tungsten phase and face centered cubic Fe3Ni2 solid solution phase. With the increase of sintering temperature, the fracture morphology of tungsten alloy is transformed from intergranular brittle fracture to transgranular brittle fracture, dimple ductile fracture, bonding phase tearing ductile fracture and transgranular brittle fracture subsequently during the sintering temperature range from 1 360 to 1 460℃.
参考文献
| [1] | L Ding;D.P. Xiang;C. Li .Effects of sintering temperature on fine-grained tungsten heavy alloy produced by high-energy ball milling assisted spark plasma sintering[J].International Journal of Refractory Metals & Hard Materials,2012(Jul.):65-69. |
| [2] | 范景莲,龚星,祁美贵,刘涛,黄伯云.细晶钨合金的制备与动态失效行为[J].中国有色金属学报,2009(12):2143-2148. |
| [3] | Das, J.;Appa Rao, G.;Pabi, S.K. .Microstructure and mechanical properties of tungsten heavy alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2010(29/30):7841-7847. |
| [4] | 王玉金,张太全,周玉,雷廷权,宋桂明.钨合金的设计窗口研究进展[J].稀有金属材料与工程,2009(z1):65-70. |
| [5] | Zhang Ke;Ge Chang Chun .Powder Metallurgy of Tungsten Alloy[J].Materials Science Forum,2007(26 Pt.2):1285-1288. |
| [6] | ARORA A;GOPAL R V G .Tungsten heavy alloy for defence applications[J].MATERIALS TECHNOLOGY,2004,19(04):210-216. |
| [7] | Guneet Sethi;Seong Jin Park;John L. Johnson .Linking homogenization and densification in W-Ni-Cu alloys through master sintering curve (MSC) concepts[J].International Journal of Refractory Metals & Hard Materials,2009(4):688-695. |
| [8] | Kyong H. Lee;Seung I. Cha;Ho J. Ryu;Soon H. Hong .Effect of two-stage sintering process on microstructure and mechanical properties of ODS tungsten heavy alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2007(1/2):323-329. |
| [9] | J.S.C. Jang;J.C. Fwu;L.J. Chang .Study on the solid-phase sintering of the nano-structured heavy tungsten alloy powder[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2007(0):367-370. |
| [10] | LI Xiao-qiang,XIN Hong-wei,HU Ke,LI Yuan-yuan.Microstructure and properties of ultra-fine tungsten heavy alloys prepared by mechanical alloying and electric current activated sintering[J].中国有色金属学报（英文版）,2010(03):443-449. |
| [11] | Jianpeng Zou;Li'e Chen .Residual stress relaxation of hydroxyapatite/316L asymmetrical functionally gradient material fabricated by hot-pressing[J].International Journal of Materials Research,2012(8):1052-1057. |
| [12] | 黄培云.粉末冶金原理[M].冶金工业出版社,2008 |
| [13] | 胡可,李小强,杨超,李元元.W-Ni-Fe合金的放电等离子烧结致密化与微观组织演变[J].中国有色金属学报（英文版）,2011(03):493-501. |
| [14] | M. Bahgat;Min-Kyu Paek;Jong-Jin Pak .Reduction investigation of WO_3/NiO/Fe_2O_3 and synthesis of nanocrystalline ternary W-Ni-Fe alloy[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2009(1/2):314-318. |
| [15] | X. Gong;J.L Fan;F. Ding .Effect of tungsten content on microstructure and quasi-static tensile fracture characteristics of rapidly hot-extruded W-Ni-Fe alloys[J].International Journal of Refractory Metals & Hard Materials,2012(Jan.):71-77. |
| [16] | Islam S. Humail;F. Akhtar;S.J. Askari .Tensile behavior change depending on the varying tungsten content of W-Ni-Fe alloys[J].International Journal of Refractory Metals & Hard Materials,2007(5/6):380-385. |
| [17] | NOH J W;KIM E P;SONG H S;BAEK W H,CHURN K S,KANG S J L .Matrix penetration of W/W grain boundaries and its effect on mechanical properties of 93W-5.6Ni-1.4 Fe heavy alloy[J].Metallurgical Transactions A,1993,24(11):2411-2416. |
| [18] | Xianghong Zhang;Yanhui Wang;Jing Lu .Wettability and reactivity in diamond-borosilicate glass system[J].International Journal of Refractory Metals & Hard Materials,2010(2):260-264. |
| [19] | O. I. Get'man;V. V. Panichkina;P. Ya. Radchenko .DIFFUSION PROCESSES AND STRUCTURIZATION IN MICROWAVE SINTERING OF BaTiO_3-SrTiO_3 AND Al_2O_3-Cr_2O_3 POWDER SYSTEMS WITH COMPLETE MISCIBILITY[J].Powder Metallurgy and Metal Ceramics,2009(5/6):279-289. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%