以乙二醇和L-乳酸熔融直接缩聚制备双端羟基聚L-乳酸预聚物(PLLA),并用1H、13C-NMR、DSC、XRD对PLLA结构和性能分析表征.以液化二苯基甲烷二异氰酸酯(MDI)为偶联剂,端羟基聚L-乳酸和端羟基聚丁二烯(HTPB)偶联反应制备橡胶改性聚乳酸基聚氨酯弹性体,并用FT-IR,1H、13C-NMR对聚合产物进行结构表征确认.DSC测试结果表明聚氨酯有聚丁二烯段和聚乳酸段两个玻璃化转变温度,熔融温度基本在130℃.随着聚丁二烯含量的增加,结晶衍射峰逐渐消失,聚氨酯的拉伸强度降低,断裂伸长率增加.断面扫描电镜结果显示聚氨酯呈微相分离结构和弹性断裂.
参考文献
| [1] | 李孝红;袁明龙;熊成东.[J].高分子通报,1999(01):24-32. |
| [2] | Okada M .[J].Progress in Polymer Science,2002,27:87-133. |
| [3] | Teng CQ;Kai Y;Ping J;Yu MH .Synthesis and characterization of poly(L-lactic acid)-poly(epsilon-caprolactone) multiblock copolymers by melt polycondensation[J].Journal of Polymer Science, Part A. Polymer Chemistry,2004(20):5045-5053. |
| [4] | Bogaert JC.;Coszach P. .Poly(lactic acids): A potential solution to plastic waste dilemma[J].Macromolecular symposia,2000(0):287-303. |
| [5] | Drumright RE.;Henton DE.;Gruber PR. .Polylactic acid technology[J].Advanced Materials,2000(23):1841-1846. |
| [6] | Hiljanenvainio M.;Hiltunen K.;Seppala JV.;Kylma J. .IMPACT MODIFICATION OF LACTIC ACID BASED POLY(ESTER-URETHANES) BY BLENDING[J].Journal of Applied Polymer Science,1997(10):1335-1343. |
| [7] | 钟伟;戈进杰;马敬红 等.[J].复旦学报(自然科学版),1999,38(06):705-708. |
| [8] | 梁宝峡,刘朋生,彭志平,陈少军.端羟基聚乳酸改性HTPB/液化MDI型聚氨酯的研究[J].弹性体,2004(03):10-13. |
| [9] | 杨凯,季平,滕翠青,徐银宝,余木火.熔融缩聚法制备聚乳酸及其聚己内酯多元醇扩链研究[J].高分子材料科学与工程,2005(02):128-131. |
| [10] | Hiltunen K;Harkonen M;Seppala et al.[J].Macromolecules,1996,29:8677-8682. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%