对高牌号无取向硅钢进行异步轧制,然后在不同时间下进行再结晶退火,研究异步轧制条件下高牌号无取向硅钢再结晶织构随退火时间的演变过程,探讨高牌号无取向硅钢再结晶织构的形成及再结晶织构组分与磁性的关系.结果表明:在750℃再结晶退火过程中,随着退火时间的延长,α织构强度减弱,织构组分逐渐向{111} <112>附近聚集,铁损逐渐下降.快慢辊侧再结晶织构类型基本相同,但慢辊侧强度高于快辊侧.

Evolution of recrystallization structure and texture of non-oriented high silicon steel after asynchronous cold rolling was studied after annealing for different time.The formation of recrystallization texture and the relation of recrystalization texture component with magnetic property of non-oriented high silicon steel were also discussed.The results ahow thata texture intensity decreases and texture component gradually accumulates around {111} <112> with the increase of annealing time at temperature of 750 ℃ , as a result core loss decreases correspondingly.It is found that recrystallization texture is same on both fast and slow roller sides, while the intensity of texture for slow roller side is higher than that for fast roller side.

参考文献

[1] 朱泉 .异步轧制实验研究[J].钢铁,1980,15(06):1-6.
[2] 张德芬 .3104铝合金形变与再结晶过程中织构及显微组织的研究[D].沈阳:东北大学,2004.
[3] Kubota T;Fujikura M;Uahigami Y .Recent progress and future trend on grain-oriented silicon steel[J].Journal of Magnetism and Magnetic Materials,2000,215 -216:39-73.
[4] Liang Z;Xu J;Wang F.Determination of ODF of polycryatalline materials from incomplete pole figures[A].Tokyo:ISIJ,1981
[5] 毛为民;赵新兵.金属的再结晶与晶粒长大[M].北京:北京科技大学出版社,1994
[6] 高秀华,齐克敏,叶何舟,邱春林.异步轧制对硅钢极薄带三次再结晶的影响[J].材料科学与工艺,2005(04):384-386.
[7] Mineo Muraki;Tetsuo Toge;Kei Sakata et al.Formation mechanism of {111} recrystallization texture in ferritic steel[J].Iron & Steel,1999,85(10):41-447.
[8] 赵骧,何长树,徐俊,左良.退火时间对IF深冲钢板再结晶织构的影响[J].东北大学学报(自然科学版),2006(12):1343-1346.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%