以阳极氧化法制得的TiO2纳米管阵列为前驱体,用浸渍法制备了不同铜掺杂量的TiO2纳米管阵列.采用场发射扫描电镜(FE-SEM)、X射线衍射(XRD)、X光电子能谱(XPS)、荧光光谱(PL)对样品进行表征.以Cr6+水溶液为目标污染物,对比不同铜掺杂量TiO2纳米管阵列的光电催化还原效果.结果表明,掺杂前后TiO2纳米管阵列在形貌上没有明显变化;掺杂的铜是以Cu2+的形态存在;掺铜后TiO2纳米管阵列还原效果优于掺铜前;低剂量铜掺杂的TiO2纳米管阵列的还原效果优于高剂量铜掺杂的TiO2纳米管阵列.
参考文献
| [1] | Quan X;Ruan X L;Zhao H M et al.[J].Environmental Pollution,2007,147:409-414. |
| [2] | 李晓平;徐宝琨;刘国范 等.[J].功能材料,1999,30(03):242-245. |
| [3] | 刘平,林华香,付贤智,孟春.掺杂TiO2光催化膜材料的制备及其灭菌机理[J].催化学报,1999(03):325-328. |
| [4] | 王浩,赵文宽,方佑龄,王润帮,李莉.二氧化钛光催化杀灭肿瘤细胞的研究[J].催化学报,1999(03):373-374. |
| [5] | Cai R;Hashimoto K;Itoch K et al.[J].Bulletin of the Chemical Society of Japan,1991,64(04):1268-1273. |
| [6] | Mane RS;Hwang YH;Lokhande CD;Sartale SD;Han SH .Room temperature synthesis of compact TiO2 thin films for 3-D solar cells by chemical arrested route[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2005(1/3):271-278. |
| [7] | Rella R;Spadavecchia J;Manera MG;Capone S;Taurino A;Martino M;Caricato AP;Tunno T .Acetone and ethanol solid-state gas sensors based on TiO2 nanoparticles thin film deposited by matrix assisted pulsed laser evaporation[J].Sensors and Actuators, B. Chemical,2007(2):426-431. |
| [8] | 李振华,刘中清,燕青芝,王宜超,葛昌纯.合成温度对二氧化钛纳米管的影响[J].功能材料,2007(03):485-487,491. |
| [9] | 刘磊,赵欣,郑铮,朱劲松.碳纳米管复合材料及其在光通信中的应用[J].光通信技术,2009(06):47-50. |
| [10] | 刘芬,徐克花.碳纳米管在生物化学传感及生物传输方面的应用[J].化学分析计量,2009(01):83-86. |
| [11] | Lu N;Zhao H M;Li J Y et al.[J].Separation and Purification Technology,2008,62:668-673. |
| [12] | Wang X;Zhao H M;Quan X et al.[J].Journal of Hazardous Materials,2009,166:547-552. |
| [13] | 石健,李军,蔡云法.具有可见光响应的C、N共掺杂TiO2纳米管光催化剂的制备[J].物理化学学报,2008(07):1283-1286. |
| [14] | 倪守高,王玲,薛建军,孙海波,雷斌,金丹萍.载Pt-TiO2纳米管阵列制备及其光电催化性能[J].材料科学与工程学报,2008(04):579-581,588. |
| [15] | 宁成云,王玉强,郑华德,谭帼馨,陈晓峰,马强,刘绪建.Cu掺杂二氧化钛纳米管阵列的研究[J].硅酸盐通报,2009(04):775-778. |
| [16] | 林雨露.掺铜TiO2光催化降解活性艳红X-3B的研究[J].江汉大学学报（自然科学版）,2009(01):37-40. |
| [17] | Gang Li;Zhong-Qing Liu;Jing Lu;Lei Wang;Zhao Zhang .Effect of calcination temperature on the morphology and surface properties of TiO_2 nanotube arrays[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2009(16):7323-7328. |
| [18] | Li K R;Wang Y J;Wang S R et al.[J].Journal of Natural Gas Chemistry,2009,18(04):449-452. |
| [19] | Chen X B;Burda C .[J].Journal of Physical Chemistry B,2004,108:15446-15449. |
| [20] | 吴树新,尹燕华,马智,秦永宁,何菲,齐晓周.掺铜方法对二氧化钛光催化氧化还原性能的影响[J].河北大学学报(自然科学版),2005(05):486-494. |
| [21] | Knorr F J;Mercado C C;McHale J L .[J].Journal of Physical Chemistry C,2008,112(33):12786-12794. |
| [22] | Das D P;Parida K;D B R et al.[J].Journal of Molecular Catalysis A:Chemical,2006,245:217-224. |
| [23] | 曾炽涛,陈爱平,陈爱华,刘伟,刘威.负载型光催化剂还原Cr6+的研究[J].华东理工大学学报(自然科学版),2003(03):277-280. |
| [24] | 鲁秀国,翟永青,丁士文,赵文革.二氧化钛光催化还原Cr（Ⅵ）的研究[J].河北大学学报（自然科学版）,2000(01):33-37. |
| [25] | 高飞,吴再华,刘晓艳.掺铜TiO2薄膜的制备及结构与光学性能的研究[J].半导体光电,2009(01):87-89,98. |
| [26] | 冯良荣,吕绍洁,邱发礼.过渡元素掺杂对纳米TiO2光催化剂性能的影响[J].化学学报,2002(03):463-467. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%