采用X射线衍射仪(XRD),扫描电子显微镜(SEM),维氏硬度计,电子万能材料试验机,动态热模拟机研究了稀土/MoSi2复合材料的结构、形貌、硬度、断裂韧性、高温屈服强度、强韧化机理等.结果表明:在MoSi2中添加适量的La2O3,可起到室温强韧化和高温强化作用.随着La2O3含量的增加,样品的硬度、断裂韧性呈先增后减的规律,其最大值分别为10.85 GPa,7.25 MPa·m1/2.该材料的强化机制为细晶和优化晶界强化;韧化机制为细晶韧化,裂纹偏转、微桥接和弯曲韧化.
参考文献
| [1] | Petrovic J J;Vasudewan A K .[J].Materials Science and Engineering,1999,A261:1. |
| [2] | Niihara K;Suzuki Y .[J].Materials Science and Engineering,1999,A261:6. |
| [3] | 张小立,吕振林,金志浩.无压反应烧结MoSi2-SiCp复相材料的制备与性能[J].稀有金属材料与工程,2003(12):1037-1040. |
| [4] | 马勤,王翠霞,薛群基.钼硅混合粉末在机械合金化过程中的结构演变[J].稀有金属材料与工程,2003(03):170-172. |
| [5] | Suzuke Y;Sekino T;Niihara K .[J].Scripta Metallurgica et Materialia,1995,33(01):69. |
| [6] | Vasudevan A K;Petrovic J J .[J].Materials Science and Engineering,1992,A 155:1. |
| [7] | Sadananda K;Feng C R;Mitra R .[J].Materials Science and Engineering,1999,A216:223. |
| [8] | Petrovic J J .[J].Materials Science and Engineering,1995,A192/193:31. |
| [9] | Hebsur M G .[J].Materials Science and Engineering,1999,A216:24. |
| [10] | Yanigibara K;Maruyama T;Nagata K .[J].Intermetallics,1996,4:133. |
| [11] | Jeng Y L;Lavernia E J J .[J].Materials Science and Engineering,1994,A189:257. |
| [12] | Schwarz R B;Srinivasan S R;Petrovic J J et al.[J].Materials Science and Engineering,1992,A155:75. |
| [13] | 刘伯威,潘进,樊毅,张金生.SiC颗粒强韧化MoSi2复合材料[J].复合材料学报,2002(01):59-63. |
| [14] | 肖纪美.金属的韧性与韧化[M].上海:上海科学技术出版社,1983:156. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%