为了提高高品质液压油缸的耐磨性能,使用45钢作为模拟材料,采用YLR-4000型光纤激光器在其表面进行激光熔覆,制备NiCrMn+WC复合涂层。利用金相显微镜(OM)和扫描电镜(SEM)分析其显微组织和微观形貌,利用X线衍射仪及能谱分析涂层的相结构和成分,并测量了其硬度以及磨损性能,获得最优的工艺参数。结果表明:激光熔覆层的致密度良好,无明显的孔洞出现;熔覆层硬度较基体的提高3~5倍,且在一定范围内,随着扫描速度的增加以及扫描功率的减少,熔覆层的硬度强化效果明显;硬质相的加入使其表面的耐磨性显著提高,在扫描速度为360 mm/min,功率为2.5 kW,WC含量为30%(质量分数)时,熔覆层的各项性能达到最优。
In order to improve the wear resistance of high-quality hydraulic cylinder, 45 steels were used as the simulative materials, the surface layers NiCrMn-WC composite coatings were fabricated by laser cladding. The microstructure and morphology were analyzed by optical microscopy (OM) and scanning electron microscopy (SEM), the phases and component elements were analyzed by X-ray diffractometry (XRD) and energy dispersive spectrometry (EDS), the microhardness and wear-resistance were tested, and the optimal parameters were obtained. The results show that the appropriate treatment parameters result in good performance of the clad layers with no defects, the microhardness of the CZ is 3-5 times larger than that of the substrate, and the microhardness is promoted as the power reducing and the scanning speed increasing, the wear-resistance is improved with the hard phases adding, each property comes to the best when the power is 2.5 kW, the scanning speed is 360 mm/min and the WC content is 30%(mass fraction).
参考文献
[1] | 冯刚.瓦楞单面机液压油缸的失效分析及改进[J].润滑与密封,2009(01):99-100,103. |
[2] | 何智,高超,王三俊,高永卫,王广军.AV90-2轴流压缩机轴承座漏油故障分析及处理[J].润滑与密封,2006(01):132-133,136. |
[3] | 张松,张春华,康煜平,吴维,王茂才,文交/力忠.钛合金表面激光熔覆原位生成TiC增强复合涂层[J].中国有色金属学报,2001(06):1026-1030. |
[4] | 马乃恒,梁工英,苏俊义.激光熔覆工艺参数对TiCp/Al表层复合材料的影响[J].中国有色金属学报,2001(06):1041-1044. |
[5] | Jiaoxi Yang;Falan Liu;Xuanhe Miao;Feng Yang .Influence of laser cladding process on the magnetic properties of WC-FeNiCr metal-matrix composite coatings[J].Journal of Materials Processing Technology,2012(9):1862-1868. |
[6] | Hemmati, I.;Ocelík, V.;De Hosson, J.T.M. .The effect of cladding speed on phase constitution and properties of AISI 431 stainless steel laser deposited coatings[J].Surface & Coatings Technology,2011(21/22):5235-5239. |
[7] | Man HC;Zhang S;Cheng FT;Guo X .In situ formation of a TiN/Ti metal matrix composite gradient coating on NiTi by laser cladding and nitriding[J].Surface & Coatings Technology,2006(16/17):4961-4966. |
[8] | L. St-Georges .Development and characterization of composite Ni-Cr + WC laser cladding[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2007(1/6):562-566. |
[9] | 王义厢,李宝增,宫耀华,程占保.45钢表面激光熔覆铁基合金涂层显微组织与性能[J].热加工工艺,2008(21):131-133. |
[10] | 张永康.激光加工技术[M].北京:化学工业出版社,2004 |
[11] | 杨胶溪,左铁钏,王喜兵,闫婷,刘华东.激光熔覆WC/Ni基硬质合金组织结构及耐磨性能研究[J].应用激光,2008(06):450-454. |
[12] | Zhou, S.;Dai, X.;Zheng, H. .Microstructure and wear resistance of Fe-based WC coating by multi-track overlapping laser induction hybrid rapid cladding[J].Optics & Laser Technology,2012(1):190-197. |
[13] | Yuling Yang;Duo Zhang;Wei Yan;Yiran Zheng .Microstructure and wear properties of TiCN/Ti coatings on titanium alloy by laser cladding[J].Optics and Lasers in Engineering,2010(1):119. |
[14] | Bao RL;Yu HJ;Chen CZ;Qi B;Zang LJ .Development of laser cladding wear-resistant coating on titanium alloys[J].Surface review and letters,2006(5):645-654. |
[15] | Bao RL;Yu HJ;Chen CZ;Qi B;Zang LJ .Development of laser cladding wear-resistant coating on titanium alloys[J].Surface review and letters,2006(5):645-654. |
[16] | 魏仑 .激光熔覆镍基金属陶瓷涂层的研究[D].昆明理工大学,2001. |
[17] | Zhiyong He;Jinxiang Zhao;Zhong Xu .Plasma surface alloying of spheroidal graphite iron[J].Surface & Coatings Technology,2000(1/3):574-578. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%