采用示波冲击法测定了9Ni钢冲击过程中裂纹萌生、扩展等阶段所消耗的能量,并通过测定钢中回转奥氏体含量,研究了冲击断裂过程中回转奥氏体的作用机制.结果表明:随着回转奥氏体含量的增加,裂纹形核功不断上升,但趋势减缓,而裂纹扩展功则先快速上升后又大幅下降,峰值与回转奥氏体稳定性的峰值重合,表明稳定性差的回转奥氏体会导致扩展功大幅下降.由于裂纹形核功随回转奥氏体稳定性的变化相对平缓,扩展功的变化则更为剧烈,因此提高回转奥氏体稳定性进而增加扩展功是改善9Ni钢低温韧性的有效手段.
参考文献
| [1] | Nakada N;Syarif J;Tsuchiyama T et al.Improvement of strength-ductility balance by copper addition in 9% Ni steels[J].Materials Science and Engineering A,2004,374(1-2):137-144. |
| [2] | Strife J R;Passoja D E J;R.Strife .The effect of heat treatment on microstructure and cryogenic fracture properties in 5Ni and 9Ni steel[J].Metallurgical Transactions A,1980,11(08):1341-1350. |
| [3] | Fultz B;Morris J W .A m(o)ssbauer spectrometry study of the mechanical transformation of precipitated austenite in 6Ni steel[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1985,16:173-177. |
| [4] | 杨跃辉,蔡庆伍,武会宾,王华.两相区热处理过程中回转奥氏体的形成规律及其对9Ni钢低温韧性的影响[J].金属学报,2009(03):270-274. |
| [5] | 雷鸣;郭蕴宜 .9Ni钢中沉淀奥氏体的形成过程及其在深冷下的表现[J].金属学报,1989,25A(01):13-17. |
| [6] | 孙树文;雷廷权;唐之秀 等.示波冲击试验评价正火12 Co1 MoV钢回火脆化敏感性[J].材料科学与工艺,1997,5(02):33-39. |
| [7] | Rautioaho R;Karjalainen P .Stress response of barkhausen noise and coercive force in 9Ni steel[J].Journal of Magnetism and Magnetic Materials,1987,68:321-327. |
| [8] | 李华瑞.材料X射线衍射分析使用方法[M].北京:冶金工业出版社,1994:39-48. |
| [9] | G. Lacroix;T. Pardoen;P.J. Jacques .The fracture toughness of TRIP-assisted multiphase steels[J].Acta materialia,2008(15):3900-3913. |
| [10] | 杨跃辉,武会宾,蔡庆伍,程莉.9Ni钢中回转奥氏体的形成规律及其稳定性[J].材料热处理学报,2010(03):73-77. |
| [11] | 于在松,范长信,刘江南,王弘喆,王正品,石崇哲.示波冲击试验中裂纹生长与扩展机理研究[J].铸造技术,2008(05):617-621. |
| [12] | GB/T 19748-2005.钢材夏比V型缺口摆锤冲击试验仪器化试验方法[S].北京:中国标准出版社,2005. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%