用等离子喷涂工艺在Q235钢基体上制备Cr2O3陶瓷涂层，并采用磷酸铝和环氧树脂对其进行封孔处理。利用图像分析法和电化学方法对封孔前后涂层的孔隙率进行了测试，采用弱极化技术和电化学阻抗谱技术对封孔前后涂层的耐蚀性能进行了研究。结果表明，封孔处理提高了涂层的耐蚀性能，环氧树脂封孔涂层的耐蚀性能更优异；陶瓷涂层在腐蚀介质中耐蚀性能主要取决于涂层的孔隙率。
Cr2O3 coating was deposited on Q235 steel by means of plasma-sprayed technology, which was sealed by aluminum phosphate and epoxy resin respectively. The porosity of the coating was investigated by graph analysis and electrochemical measurement, and the corrosion resistance of the coating was characterized by polarization curve and electrochemical impedance spectroscopy (EIS). It is found that the sealing treatment can elevate corrosion resistance of the Cr2O3 coating. Compared with the coating sealed with aluminum phosphate, the epoxy resin-sealed coating shows excellent corrosion resistance. The electrochemical behavior of the Cr2O3 coating in the corrosive electrolyte depends mainly on the porosity of the coating.
参考文献
| [1] | 李守彪,许立坤,沈承金,李相波.等离子喷涂耐冲蚀陶瓷涂层的性能研究[J].中国腐蚀与防护学报,2011(03):196-201. |
| [2] | Liscano S;Gil L;Staia MH .Effect of sealing treatment on the corrosion resistance of thermal-sprayed ceramic coatings[J].Surface & Coatings Technology,2004(0):135-139. |
| [3] | 江志强,席守谋,李华伦.等离子喷涂陶瓷涂层封孔处理的现状与展望[J].兵器材料科学与工程,1999(03):56. |
| [4] | 曹国平,张登君.等离子喷涂氧化锆涂层的表面处理[J].化工冶金,1997(02):173-175. |
| [5] | 龚志强,吴子健,刘焱飞,吕艳红.激光重熔等离子喷涂Al2O3-13%TiO2涂层的组织结构[J].中国表面工程,2011(01):12-15. |
| [6] | 杨海钢,朱雪梅,雷明凯.腐蚀电化学方法评价硬质涂层孔隙率[J].腐蚀科学与防护技术,2005(06):413-417. |
| [7] | 贾志军,李晓刚,杜翠薇.电位扫描速率对电极过程动力学参数测试结果的影响[J].腐蚀与防护,2010(11):829-832. |
| [8] | 郭金花,吴嘉伟,倪晓俊,李德仁,连法增,卢志超.电弧喷涂含非晶相的Fe基涂层的电化学行为[J].金属学报,2007(07):780-784. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%