Effects of Mo Contents in Matrix on Microstructure and Properties of Vanadium Carbide Coating Formed by Thermal Diffusion Treatment

^1, , ^2,

1.School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China

2.School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China

基金项目: Item Sponsored by National Natural Science Foundation of China (50671012)

1.School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China

2.School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China

[1]	Q.B.Zhang;L.Li;S.H.Li;R.Huang .[J].Physical Testing and Chemical Analysis Part A:Physical Testing,2004,40:202-204.
[2]	Z.Z.Zhou;D.J.Kong;F.Yuan;Y.F.Yan .[J].Die & Mould Industry,2010,36(04):63-67.
[3]	L.W.Tang;M.B.Yang;W.L.Zhao;H.Yang,Z.F.Sun .[J].Die & Mould Manufacture,2007,7(09):70-72.
[4]	C.K.N.Oliveira;C.L.Benassi;L.C.Casteletti .[J].Surface and Coatings Technology,2006,201:1880-1885.
[5]	S.M.Hao;R.Y.Sun .[J].Acta Metall Sinica,1989,2:375-379.
[6]	D.J.Kong;C.Z.Zhou .[J].J China Univ Min Tech,2011,40:162-166.
[7]	Z.P.Wang .[J].Hot Working Technology,2011,40(16):161-163.
[8]	X.J.Liu;H.C.Wang .[J].Trans Mater Heat Treat,2010,31:150-154.
[9]	X.J.Liu;H.C.Wang;D.W.Li;Y.X.Wu .[J].Trans Mater Heat Treat,2006,27:119-122.
[10]	S.H.Wang;S.T.Jin .[J].J Hebei Inst Tech,1998,20:8-14.
[11]	L.Liu;L.Lin;S.F.Zhao .[J].Hot Working Technology,1994,23(03):32-34.
[12]	T.Arai;H.Fujita;Y.Sugimoto;Y.Ohta .[J].Industrial Heating,1986,53(09):26-28.

上一张下一张

计量

作者相关

文章评分

材料期刊网