采用TEM、SEM和EBSD等组织分析技术研究了β退火态片层组织TC11钛合金两相区热变形球化过程中组织的精细结构和晶界特征.结果表明,片层组织的球化过程包括α片内小角度晶界形变和回复亚结构的形成、β相沿亚晶界扩散和晶界滑动作用下片层的解体以及晶界扩散和滑动驱动下α晶粒的球化和组织的均匀化.EBSD测试结果揭示了片层组织两相区热变形的球化机制为α相的连续动态再结晶和β相的动态回复或不连续动态再结晶过程.
参考文献
| [1] | 曾卫东,周义刚.冷速对TC11合金β加工显微组织和力学性能的影响[J].金属学报,2002(12):1273-1276. |
| [2] | 陈慧琴,林好转,郭灵,曹春晓.钛合金热变形机制及微观组织演变规律的研究进展[J].材料工程,2007(01):60-64. |
| [3] | Seshacharyulu T;Medeiros S C;Morgan J T;Malas J C;Frazier W G;Prasad Y V R K .Hot deformation mechanisms in ELI grade Ti-6Al-4V.[J].Scripta materialia,1999(3):283-288. |
| [4] | Seshacharyulu T;Medeiros S C;Morgan J T et al.[J].Materials Science and Engineering,2000,A279:289. |
| [5] | Seshacharyulu T;Medeiros S C;Frazier W G et al.[J].Materials Science and Engineering,2002,A325:112. |
| [6] | Semiatin S L;Seetharaman V;Weiss I.[J].JOM-Journal of the Minerals Metals and Materials Society,1997(06):33. |
| [7] | Semiain S L;Seetharaman V;Weiss I.Advances in the Science and Technology of Titanium Alloy Processing[M].USA:The Minerals,Metals & Materials Society,1997:3. |
| [8] | Salishchev G A;Zerebtsov S V;Mironov S Y.[J].Materials Science Forum,2004(467-470):501. |
| [9] | 孙新军 .钛合金片层组织的等轴化规律及超细晶钛合金超塑性的研究[D].清华大学,1999. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%