研究了不同电磁组合场对AZ61镁合金凝固组织的影响.结果表明,在静磁场作用下,镁合金的凝固组织为等轴晶,晶界上的结晶相成网状分布;在静磁场与工频交流电组合场作用下,其凝固组织与只施加静磁场时类似,基本为等轴晶,但由于交流电的施加晶粒明显得到细化,晶界上结晶相的网状结构也变得细小;而在镁合金凝固过程中同时施加静磁场和直流电流组合场时,由于组合场产生的熔体内部的定向力作用的结果,凝固组织主要为蔷薇状晶粒,组织得到明显的净化,其晶界上结晶相的网状结构彻底消失,以不连续的薄条状和点状形态分布.
Solidification microstructure of AZ61 magnesium alloys with different electric-magnetic fields was studied. It was found that solidification microstructure of magnesium alloys were equiaxed grains and the Mg-Al-Zn compound phases appeared as meshes on grains boundaries under magnetostatic filed. Solidified under the magnetostatic-power current field, the microstructure was mainly consisted of equiaxed grains similar to that under the magnetostatic field. But the grains were refined obviously and the mesh structure of compound phases became fine due to the applied power current; while in the solidification process of Mg alloys under the magnetostatic-direct current field, the solidification microstructure was mainly rosette grain and purified significantly; the mesh structure of the compound phases disappeared entirely and they were distributed as discontinuous ribbons and spots; they were the results of the directional force inside melts caused by the combination fields.
参考文献
| [1] | 许光明,包卫平,郑佳伟,左玉波,崔建忠.静磁场作用下镁合金AZ61凝固过程研究[J].稀有金属,2004(01):89-92. |
| [2] | 翟春泉,曾小勤,丁文江,王渠东,吕宜振,徐小平.镁合金的开发与应用[J].机械工程材料,2001(01):6-10. |
| [3] | 刘正.镁基轻质合金理论基础及其应用[M].Beijing:Mechanical Industrial Press,2002 |
| [4] | 曾荣昌,柯伟,徐永波,韩恩厚,朱自勇.Mg合金的最新发展及应用前景[J].金属学报,2001(07):673-685. |
| [5] | Hans Conrad .[J].Materials Science and Engineering,2000,A287:205. |
| [6] | Zhang Beijiang et al.[J].J Mater Sci Technology,2002,18(05):401. |
| [7] | 姚可夫,王沛玉.脉冲电流对金属材料塑性变形和组织结构与性能的影响[J].机械强度,2003(03):340-342,346. |
| [8] | 赵红岩,石广新,翁康荣,郑飞燕,赵红亮.电磁场对AZ91镁合金凝固态组织的影响[J].轻合金加工技术,2006(08):14-16,53. |
| [9] | 包卫平,许光明,郑佳伟,崔建忠.不同磁场作用对AZ31镁合金的凝固组织的影响[J].材料与冶金学报,2003(03):216-219. |
| [10] | 韩富银,杨巧莲,高义斌,张金山,池承忠.电磁搅拌对镁合金半固态组织的影响及机理[J].铸造设备研究,2005(03):13-15. |
| [11] | 马晓东,张兴国,任政,房灿峰,郝海,金俊泽.电磁连铸过程中电磁场对变形镁合金凝固组织的影响[J].铸造,2007(09):914-917. |
| [12] | 胡汉起.金属凝固原理[M].Beijing:Mechanical Industrial Press,2000 |
| [13] | 包卫平,许光明,班春燕,崔建忠.静磁场对镁合金凝固组织的影响[J].物理学报,2004(06):2024-2028. |
| [14] | 赵凯华.电磁学[M].北京:高等教育出版社,1985 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%