通过在铸造过程中对熔体进行二元和三元变质处理,制备了硅质量分数为18%的A390过共晶铝硅合金;通过金相分析、扫描电镜观察、拉伸性能测试、耐磨性能测试等手段研究了变质处理对A390过共晶铝硅合金组织和性能的影响.结果表明:A390合金经过变质处理后,初晶硅棱角得到钝化,尺寸小于30μm,共晶硅出现球化,晶粒尺寸减小;变质后合金力学性能明显提高,其中经三元变质处理后其室温抗拉强度与伸长率较未变质处理的分别提高了31%与150%;耐磨性能也有一定程度的改善,三元变质处理后的磨损机理以微观切削为主.
The A390 hypereutectic Al-Si alloy with 18wt% Si content was prepared through the melt modified by binary and ternary modifiers during the casting process. The influence of modification on microstructure and mechanical properties of A390 hypereutectie Al-Si alloy was investigated by optical microscopy analysis, scanning electron microscopy observation, wear resistance test and tensile strength test. The results show that after the modification of A390 alloy, the comer angle of the primary Si was inactivated, and its size was below 30 μm. Eutectie Si was spheroidized, and the grain was refined. Mechanical properties of the modified alloy were improved apparently. After ternary modification; compared to non-modification, the elongation and tensile strength of A390 alloy at room temperature had been increased by 150% and 31%, respectively. Wear resistance of the A390 alloy was also improved. The wear resistance in ternary modification was mainly microscopic cutting.
参考文献
| [1] | 赖华清,赖俊传,毛高波.过共晶铝硅合金变质工艺研究[J].湖北汽车工业学院学报,1998(03):57. |
| [2] | 柳秉毅.改善铝硅铸造合金组织与性能研究的若干进展[J].南京工程学院学报（自然科学版）,2004(01):1-7. |
| [3] | 姚书芳,毛卫民,赵爱民,钟雪友.过共晶铝硅合金细化变质剂的研究[J].特种铸造及有色合金,2000(05):1-3. |
| [4] | 杨伏良,甘卫平,陈招科.高硅铝合金几种常见制备方法及其细化机理[J].材料导报,2005(05):42-45,49. |
| [5] | 乐秀伟.过共晶铝硅合金的熔炼及变质处理[J].北京理工大学学报,1995(01):61. |
| [6] | 张金山,许春香,韩富银.复合变质对过共晶高硅铝合金组织和性能的影响[J].中国有色金属学报,2002(z1):107-110. |
| [7] | 兰晔峰,郭朋,张继军.稀土对Al-Ti-B-RE中间合金细化性能的影响[J].铸造技术,2005(09):774-775,778. |
| [8] | 乔进国,刘相法,刘相俊,边秀房.Al-P中间合金的变质特性及变质机理探讨[J].内燃机配件,2003(05):18-22. |
| [9] | 欧阳志英,毛协民,唐多光,张金龙,王海江,侯旭.稀土对过共晶Al-Si合金P变质效果的影响[J].特种铸造及有色合金,2003(01):22-23. |
| [10] | 齐广慧,刘相法,杨志强,柳延辉,边秀房."绿色”高效Al -Si合金变质剂--Al-P中间合金[J].材料科学与工艺,2001(02):211-214. |
| [11] | 张蓉 .熔体过热处理对Al-Si过共晶合金凝固组织及耐磨性的影响[D].西北工业大学,2000. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%