Corrosion behavior of pure zinc and its alloy under thin electrolyte layer

金属学报(英文版), 2010, 23(6): 416-430.

^1, , ^2, , ^3, , ^4, , ^5,

1.Department of Chemistry,Zhejiang University,Hangzhou 310027,China

2.Department of Chemistry,Zhejiang University,Hangzhou 310027,China

3.Department of Chemistry,Zhejiang University,Hangzhou 310027,China

4.Department of Chemistry,Zhejiang University,Hangzhou 310027,China

5.Department of Chemistry,Zhejiang University,Hangzhou 310027,China;State Key Laboratory for Corrosion and Protection,Institute of Metal Research,Chinese Academy of Sciences,Shenyang 110016,China

基金项目: National Natural Science Foundation of China(50801056;J0830413) the National R&D Infrastructure and Facility Development Program of China(2005DKA10400-Z20)

Corrosion behavior of pure zinc and its alloy under thin electrolyte layer

Liyun ZHENG ^1, , Fahe CAO ^2, , Wenjuan LIU ^3, , Bingli JIA ^4, , Jianqing ZHANG ^5,

1.Department of Chemistry,Zhejiang University,Hangzhou 310027,China

2.Department of Chemistry,Zhejiang University,Hangzhou 310027,China

3.Department of Chemistry,Zhejiang University,Hangzhou 310027,China

4.Department of Chemistry,Zhejiang University,Hangzhou 310027,China

5.Department of Chemistry,Zhejiang University,Hangzhou 310027,China;State Key Laboratory for Corrosion and Protection,Institute of Metal Research,Chinese Academy of Sciences,Shenyang 110016,China

Keywords： Thin electrolyte layers

The corrosion behavior of zinc and its alloy under thin electrolyte layers (TEL) in 0.1M NaCl solution was investigated by cathodic polarization curves and EIS. There was only one phase in pure zinc while zinc alloy consisted of eutectic phase and primary phase. Corrosion rate of zinc alloy was faster than that of pure zinc due to the effect of the micro-galvanic couples between the primary phase and the eutectic phase.The results indicated that corrosion rate of zinc alloy was greatly enhanced under TEL than that in bulk solution. Pure zinc exhibited minimum corrosion resistance as TEL decreased to 198 μm. Zinc and its alloy exhibited localized corrosion under TEL while it was more uniform in bulk solution. There were two capacitive loops in high frequency (HF) and middle frequency (MF) respectively, with finite length diffusion in low frequency (LF) presented in EIS. For pure zinc under TEL below 300 μm an additional inductive loop presented in MF-LF. The corrosion prodncts and morphology were respectively examined by X-ray diffraction (XRD), FTIR (Fourier Transform Infra Red) and SEM-EDS. FTIR micro spectroscopy results indicated that the component of the corrosion products was similar at different section of the specimen surface but different in content.

参考文献

[1]	J. Morales;F. Diaz;J. Hernandez-Borges;S. Gonzalez .Atmospheric corrosion in subtropical areas: XRD and electrochemical study of zinc atmospheric corrosion products in the province of Santa Cruz de Tenerife (Canary Islands, Spain)[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2006(2):361-371.
[2]	G.A. EL-Mahdy .Advanced Laboratory Study on the Atmospheric Corrosion of Zinc under Thin Electrolyte Layers[J].Corrosion: The Journal of Science and Engineering,2003(6):505-510.
[3]	S. Xing;Y. Li;J. Wu;Y. Yan .Electrochemical methods study on corrosion of 5% Al-Zn alloy-coated steel under thin electrolyte layers[J].Materials and Corrosion,2010(5):428-431.
[4]	Y. Y. Chen;S. C. Chung;H. C. Shih .Studies on the initial stages of zinc atmospheric corrosion in the presence of chloride[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2006(11):3547-3564.
[5]	F. Rosalbino;E. Angelini;D. Maccio;A. Saccone;S. Delfino .Influence of rare earths addition on the corrosion behaviour of Zn-5%Al (Galfan) alloy in neutral aerated sodium sulphate solution[J].Electrochimica Acta,2007(24):7107-7114.
[6]	F. Rosalbino;E. Angelini;D. Maccio;A. Saccone;S. Delfino .Application of EIS to assess the effect of rare earths small addition on the corrosion behaviour of Zn-5%Al (Galfan) alloy in neutral aerated sodium chloride solution[J].Electrochimica Acta,2009(4):1204-1209.
[7]	N.C. Barnard;S.G.R. Brown .Modelling the relationship between microstructure of Galfan-type coated steel and cut-edge corrosion resistance incorporating diffusion of multiple species[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(10):2846-2857.
[8]	Y. Hamlaoui;F. Pedraza;L. Tifouti .Corrosion monitoring of galvanised coatings through electrochemical impedance spectroscopy[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(6):1558-1566.
[9]	L. Sziraki;E. Szocs;Zs. Pilbath;K. Papp;E. Kalman .Study of the initial stage of white rust formation on zinc single crystal by EIS, STM/AFM and SEM/EDS techniques[J].Electrochimica Acta,2001(24/25):3743-3754.
[10]	C. Cachet;F. Ganne;G. Maurin;J. Petitjean;V. Vivier;R. Wiart .EIS investigation of zinc dissolution in aerated sulfate medium. Part I: bulk zinc[J].Electrochimica Acta,2001(3):509-518.
[11]	M.C. Li;M. Royer;D. Stien;A. Lecante;C. Roos .Inhibitive effect of sodium eperuate on zinc corrosion in alkaline solutions[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(7):1975-1981.
[12]	A. P. Yadav;A. Nishikata;T. Tsuru .Evaluation of impedance spectra of zinc and galvanised steel corroding under atmospheric environments[J].Corrosion Engineering, Science and Technology,2008(1):23-29.
[13]	Z.Y. Chen;D. Persson;C. Leygraf .Initial NaCl-particle induced atmospheric corrosion of zinc-Effect of CO_2 and SO_2[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(1):111-123.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Corrosion behavior of pure zinc and its alloy under thin electrolyte layer

参考文献