研究了碘酸钾对2024铝合金表面化学镀Ni-P合金层沉积速度的影响,对镀层的表面形貌进行了观察.结果表明,碘酸钾提高了Ni-P镀层的沉积速度,且当镀液中碘酸钾含量为20 mg/L时,沉积速度达到最大值.Ni-P镀层由胞状物组成,碘酸钾使胞状物变得更加细小,胞状物间结合得更加致密、均匀,进一步提高了Ni-P镀层在3.5%NaCl溶液中的耐蚀性.
参考文献
| [1] | Zamponi C;Sonneberger S;Haaks M;Muller I;Staab T .Investigation of fatigue cracks in aluminium alloys 2024 and 6013 in laboratory air and corrosive environment[J].Journal of Materials Science,2004(23):6951-6956. |
| [2] | M. Kurt;Y. Kaynak;E. Bagci .Evaluation of drilled hole quality in Al 2024 alloy[J].The International Journal of Advanced Manufacturing Technology,2008(11/12):1051-1060. |
| [3] | Fratesi R;Bouanani M;Roventi G;Barucca G;Cherkaoui F .Microstructural characterization and corrosion resistance of Ni-Zn-P alloys electrolessly deposited from a sulphate bath[J].Journal of Applied Electrochemistry,1999(5):637-645. |
| [4] | 韩克平.巯基乙酸加速化学镀镍的机理[J].材料保护,1996(07):7. |
| [5] | 化学镀Ni-P合金中无机盐加速剂的影响[J].中国有色金属学报,1999(01):155. |
| [6] | 雷志刚,郑传明,韩荣生,朱广东,贺国旭.四种稳定剂对化学镀镍液及镀层耐蚀性的影响[J].腐蚀与防护,2007(03):135-137. |
| [7] | 胡光辉,吴辉煌,杨防祖,王森林.添加剂对化学沉积速率的影响[J].物理化学学报,2004(03):327-330. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%