通过先在水溶液中电镀Cr之后再在摩尔比为2∶l的AlCl3-EMIC(氯化1-甲基3-乙基咪唑)离子液体电镀Al的方法,在1Cr17钢表面制备出Cr/Al复合镀层.研究了在740℃条件下不同时间热处理对涂层组织和结构的影响.光学显微镜、二次电子和特征X射线能谱及X射线衍射研究结果表明:Cr/Al复合镀层通过740℃热处理可以得到Al-Cr涂层,随着时间的延长,外表面合金层成分依次按Al4Cr→Al11Cr4→Al9Cr4→Al8Cr5变化,最后形成单相的Al8Cr5,且涂层与基体之间不发生明显的互扩散;在5～20 min内Al9Cr4成分层的厚度及反应掉的Cr镀层厚度与时间平方根符合线性关系;氮气气氛中热处理可以减少涂层表面的空洞.显微硬度测试结果表明:Al8Cr5的脆性小,且硬度高于其他3种合金层.
参考文献
| [1] | M.P.Brady;B.Gleeson .Alloy design strategies for promoting protective oxide- scale formation[J].JOM,2000(1):16-21. |
| [2] | Xiang ZD;Rose SR;Datta PK;Scheeffer M .Steam oxidation resistance and thermal stability of chromium aluminide/chromium hybrid coating on alloy steels formed at low temperatures[J].Surface & Coatings Technology,2009(9):1225-1230. |
| [3] | Huttunen-Saarivirta E;Stott F H;Rohr V et al.Erosion-oxidation behavior of chromized-aluminized 9% chromium steel under fluidized-bed conditions at elevated temperature[J].Oxidation of Metals,2007,68(3 -4):113-132. |
| [4] | W. Zhou;Y.G. Zhao;Q.D. Qin .A new way to produce Al + Cr coating on Ti alloy by vacuum fusing method and its oxidation resistance[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2006(1/2):254-259. |
| [5] | Cekada, M;Panjan, M;Cimpric, D;Kovac, J;Panjan, P;Dolinsek, J;Zalar, A .Analysis of the diffusion processes in Al/Cr, Al/Fe and Cr/Fe multilayers using the MRI model[J].Vacuum: Technology Applications & Ion Physics: The International Journal & Abstracting Service for Vacuum Science & Technology,2009(1):147-151. |
| [6] | Michel Armand;Frank Endres;Douglas R. MacFarlane .Ionic-liquid materials for the electrochemical challenges of the future[J].Nature materials,2009(8):621-629. |
| [7] | 李岩,凌国平,刘柯钊,陈长安,张桂凯.铁素体不锈钢室温熔盐镀铝层的热处理[J].材料热处理学报,2009(05):182-186. |
| [8] | Okamoto H .Al-Cr (Aluminum-Chromium)[J].Journal of Phase Equilibria and Diffusion,2008,29(01):112-113. |
| [9] | Tunca N;Delamore G W;Smith R W .Corrosion of Mo,Nb,Cr,and Y in molten aluminum[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1990,21(11):2919-2928. |
| [10] | Umeda A;Yakou T;Kamasaki K et al.Structural defects formed in alloy layers of Fe-Al system by diffusion in air[J].Tetsu To Hagane-Journal of the Iron and Steel Institute of Japan,2009,95(09):645-648. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%