以莫来石纤维为增强体，采用固相烧结法制备了莫来石纤维增强多孔玻璃基复合材料。研究了烧结温度和保温时间对多孔玻璃复合材料的微观结构和性能的影响。采用SEM、XRD等检测手段对复合材料的物相结构及断面的微观形貌进行测试，采用阿基米德法测量其密度，使用万能材料试验机测量其抗折强度。结果表明，随着发泡温度升高、保温时间延长，多孔玻璃的孔径增大，但发泡温度过高或保温时间过长易产生连通孔；抗折强度、密度随着发泡温度的升高或保温时间的延长而降低。当发泡温度为840℃，保温时间为20min时，比强度达到最大值为0．013m2／s2。
Using mullite-fiber as reniforeement, the mullite-fiber-reniforced porous glass matrix composites were prepared by solid-phase sintering. The effect of sintering temperature and holding time on the mierostructure and properties of mullite-fiber-reniforced porous glass matrix composites were researched in detail. The struc- tures and fracture surface morphologies of the composites were characterized by XRD and SEM analyses, the density were tested by the archimedean method. The flexural property of the composites were tested by a uni- versal testing machine. The results show that with the foaming temperature or holding time increased, the aper- ture size of porous glass was increased too, but it will form interconnect hole when the foaming temperature was too high or holding time was too long; the flexural strength and the density reduce with the increase of foaming temperature and holding time; the maximum specific strength was 0. 013m2/s2 when the foaming temperature was 840℃ and the holding time was 20min.
参考文献
| [1] | 薛明,周大利,曹巨辉,汪宏涛,杨为中.磷灰石-硅灰石多孔玻璃陶瓷的制备与晶相结构研究[J].功能材料,2009(01):97-100. |
| [2] | Nimjaroen, C;Morimoto, S;Tangsathitkulichai, C .Preparation and properties of porous glass using fly ash as a raw material[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2009(34/36):1737-1741. |
| [3] | Sarika Mishra;R. Mitra;M. Vijayakumar .Structure and properties of short fibre reinforced silica matrix composite foams[J].CERAMICS INTERNATIONAL,2009(8):3111-3116. |
| [4] | Francois Mear;Pascal Yot;Martine Cambon;Renaud Caplain;Michel Ribes .Characterisation of porous glasses prepared from Cathode Ray Tube (CRT)[J].Powder Technology: An International Journal on the Science and Technology of Wet and Dry Particulate Systems,2006(1):59-63. |
| [5] | Bernardo E;Cedro R;Florean M et al.[J].Ceramics International,2007,33(06):963-968. |
| [6] | Hrma, P .Effect of heating rate on glass foaming: Transition to bulk foam[J].Journal of Non-Crystalline Solids,2009(4/5):257-263. |
| [7] | 潘守芹.新型玻璃[M].上海:同济大学出版社,1992:80-115. |
| [8] | Yong Liu;Yanni Tan;Ting Lei;Qijun Xiang;Yunjuan Han;Baiyun Huang .Effect of porous glass-ceramic fillers on mechanical properties of light-cured dental resin composites[J].Dental materials,2009(6):709-715. |
| [9] | Rozenst rauha I;Cimdins R .[J].Glass Sci Tech,2002,75(03):132-138. |
| [10] | Mear F;Yot P;Ribes M .[J].Materials Let ters,2006,60(07):929-934. |
| [11] | 高淑雅,郭晓琛,郭宏伟,殷海荣,田鹏.莫来石纤维增强多孔玻璃基复合材料的结构与性能[J].功能材料,2010(08):1465-1468. |
| [12] | Kiyoshi Okada;Fumihiko Ikawa;Toshihiro Isobe .Low temperature preparation and machinability of porous ceramics from talc and foamed glass particles[J].Journal of the European Ceramic Society,2009(6):1047-1052. |
| [13] | Ha J S;Chawla K K .[J].Materials Science and Engineering,1995,122(A203):171-176. |
| [14] | Chawlaa N;Chawla K K .[J].Composites Science and Technology,2001,61(13):1923-1930. |
| [15] | 郭宏伟,刘新年,郭宏武,陈真真.高密度泡沫玻璃的制务工艺及性能研究[J].新型建筑材料,2009(06):42-44. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%