将氰化镧溶解到AlCl3-EMIC室温离子液体(N=0.667)中,制备氯化镧饱和的AlCl3-EMIC离子液体;采用循环伏安法、计时电流法研究了在饱和LaCl3-AlCl3-EMIC中钨电极上的阴极过程和成核机理;并在不同的电流密度下制备了镀层,利用扫描电镜对镀层表面形貌进行了分析.结果表明:氯化镧的加入使得铝的沉积电位负移,由拟合曲线可知其成核过程为三维瞬时形核,在12 mA/cm2的电流密度下可以获得光滑致密的镀层,氯化镧的加入可以细化晶粒.
参考文献
| [1] | 刘建国,李治国,田鹏,宋溪明,刘振荣,杨家振.一种新的绿色溶剂--室温离子液体[J].辽宁大学学报(自然科学版),2003(02):179-184. |
| [2] | Jiang T;Brym MJC;Dube G;Lasia A;Brisard GM .Electrodeposition of aluminium from ionic liquids: Part I - electrodeposition and surface morphology of aluminium from aluminium chloride (AlCl3)-l-ethyl-3-methylimidazolium chloride ([EMIm]Cl) ionic liquids[J].Surface & Coatings Technology,2006(1/2):1-9. |
| [3] | Aravinda CL;Burger B;Freyland W .Nanoscale electrodeposition of Al on n-Si(111): H from an ionic liquid[J].Chemical Physics Letters,2007(4-6):271-275. |
| [4] | Mukhopadhyay I;Aravinda C L;Borissov D et al.[J].Electrochimica Acts,2005,50:1275. |
| [5] | Chiacheng Tai;Fanyin Su;Iwen Sun .[J].Electrochimica Acta,2005,50:55u4. |
| [6] | Po-Yu Chena;Charles L Hussey .[J].Electrochimica Acta,2007,52:1857. |
| [7] | Tetsuya Tsuda;Toshiyuki Nohira;Yasuhiko Ito .Electrodeposition of lanthanum in lanthanum chloride saturated AlCl_3-1-ethyl-3-methylimidazolium chloride molten salts[J].Electrochimica Acta,2001(12):1891-1897. |
| [8] | 王喜然,华一新.绿色电解液--离子液体电解铝的研究现状[J].云南冶金,2007(03):28-31. |
| [9] | 孙淑萍,李东春.铝在室温熔盐中的电沉积[J].轻合金加工技术,2003(11):28-30. |
| [10] | Zhao Y et al.[J].Electrochimica Acta,1997,42:1639. |
| [11] | 周绍民.金属的电沉积原理及研究方法[M].上海:上海科学出版社,1982 |
| [12] | 李军,李冰.LiF-NaF-KF-K2TiF6熔盐中Ti（Ⅳ）的电化学还原及电结晶过程[J].稀有金属材料与工程,2007(01):15-19. |
| [13] | 杨防祖.纯钯电沉积及其成核机理研究[J].电化学,1997(01):103. |
| [14] | 吴辉煌.电化学应用基础[M].厦门:厦门大学出版社,2006 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%