采用高纯(6mol/L)Ge、Zn、P单质为原料,按化学计量比并富P 0.2%配料,通过双温区法合成ZnGeP2多晶粉料,再用水平温梯冷凝法(HGF)生长出尺寸达10mm×20mm×80mm的单晶棒.对单晶进行了X射线衍射、红外透过率、热导率等测试,测试结果表明;单晶完整性好,红外透过率较高;5mm厚晶片(未退火、镀膜)在2～8μm范围内平均透过率可达54%以上;在室温附近(297.34K)热导率为35.89W/(m·K).
参考文献
| [1] | Schunemann P G;Budni P A;Pomeranz L.Advanced Solid State Lasers(ASSL)Orlando[M].Florida:Optical Society of America,1997:253-255. |
| [2] | Zawilski KT;Schunemann PG;Setzler SD;Pollak TM .Large aperture single crystal ZnGeP2 for high-energy applications[J].Journal of Crystal Growth,2008(7/9):1891-1896. |
| [3] | Verozubova G A;Gribenyukov A I;Korotkova V V et al.[J].Journal of Crystal Growth,2000,213:334-339. |
| [4] | G. A. Verozubova;A. I. Gribenyukov;Yu. P. Mironov .Two-Temperature Synthesis of ZnGeP_2[J].Inorganic materials,2007(10):1040-1045. |
| [5] | Andreev Y M;Verozubova G A;Gribenyukov A I et al.[J].Journal of the Korean Physical Society,1998,33(03):356-361. |
| [6] | 林彦霆,顾庆天,刘宏,张怀金,葛文伟,房昌水,胡小波,王继扬.ZnGeP2多晶料合成与晶体生长[J].功能材料,2006(06):864-866. |
| [7] | 吴海信,倪友保,耿磊,毛明生,王振友,程干超,杨琳.红外非线性晶体ZnGeP2的生长及品质研究[J].人工晶体学报,2007(03):507-511. |
| [8] | Tochitsky SY;Petukhov VO;Gorobets VA;Churakov VV;Jakimovich VN .Efficient continuous-wave frequency doubling of a tunable CO2 laser in AgGaSe2[J].Applied optics,1997(9):1882-1888. |
| [9] | Kato K .Second-harmonic and sum-frequency generation in ZnGeP2[J].Applied optics,1997(12):2506-2510. |
| [10] | 黄呈辉,黄见洪,张戈,黄祥金,沈鸿元.一种精确计算光学材料吸收系数的方法[J].激光杂志,2001(06):45-46. |
| [11] | Beasley J D .[J].Applied Optics,1994,33(06):1000-1003. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%