为提高镁合金耐蚀性,在ZM6基体上采用冷喷涂技术制备了纯铝涂层.用扫描电镜(SEM)、能量色散谱(EDS)、显微硬度测试仪等研究了涂层形貌结构和性能；利用电化学方法和中性盐雾实验对涂层的抗腐蚀性能进行了评价.结果表明:在ZM6基体上冷喷涂的铝涂层结构致密,孔隙率为0.8％,显微硬度HV平均为59.8,高于镁合金；结合力达到21MPa；涂层抗腐蚀性能优于镁合金,冷喷涂铝涂层的自腐蚀电位与镁合金相比较,提高了约700mV,中性盐雾实验200h无腐蚀,可为ZM6提供长效保护.
参考文献
| [1] | 丁文江.镁合金科学与技术[M].北京:科学出版社,2007 |
| [2] | Amy L. Rudd;Carmel B. Breslin;Florian Mansfeld .The corrosion protection afforded by rare earth conversion coatings applied to magnesium[J].Corrosion Science,2000(2):275-288. |
| [3] | 王福会,杜克勤,张伟.镁合金的腐蚀与防护研究进展[J].中国材料进展,2011(02):29-34. |
| [4] | F. Gartner;T. Schmidt;T. Stoltenhoff;H. Kreye .Recent Developments and Potential Applications of Cold Spraying[J].Advanced Engineering Materials,2006(7):611-618. |
| [5] | Novoselova T;Fox P;Morgan R;O'Neill W .Experimental study of titanium/aluminium deposits produced by cold gas dynamic spray[J].Surface & Coatings Technology,2006(8):2775-2783. |
| [6] | PAPYRIN A;KOSAREV V;KLINKOV K.Cold spray technology[M].Amsterdam:Elsevier Science,2006 |
| [7] | 卜恒勇,卢晨.冷喷涂技术的研究现状及进展[J].材料工程,2010(01):94-98. |
| [8] | T. Schmidt;F. Gartner;H. Assadi .Development of a generalized parameter window for cold spray deposition[J].Acta materialia,2006(3):729-742. |
| [9] | D.Zhang,P.H.Shipway,D.G.McCartney.工艺参数变化对冷喷涂铝沉积性能的影响[J].中国表面工程,2008(04):1-7. |
| [10] | 刘道新.材料的腐蚀与防护[M].西安:西北工业大学出版社,2006:15-16. |
| [11] | 王佳杰,魏尊杰,霍树斌,王吉孝,张颖,王志平.超音速冷气动力喷涂Cu涂层的结合机理[J].焊接,2005(09):36-39. |
| [12] | 孟模,张治民,徐宏妍.热喷涂铝涂层与镁合金基体结合强度的研究[J].中北大学学报（自然科学版）,2011(03):377-381. |
| [13] | 吴子健.热喷涂技术与应用[M].北京:机械工业出版社,2007:1-5. |
| [14] | TAO Yong-shan;XIONG Tian-ying;SUN Chao et al.Micro structure and corrosion performance of cold sprayed aluminium coating on AZ91D magnesium alloy[J].Corrosion Science,2010,52(10):3191-3197. |
| [15] | 韩玮,孟宪明,赵杰,张俊宝.冷喷涂304不锈钢涂层的组织与耐磨耐蚀性能[J].材料保护,2011(03):77-80. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%