通过高能球磨制备的片状银粉将产生大量的晶体缺陷，这些缺陷的存在将影响银粉的导电性能。对高能球磨制得的片状银粉进行了热处理悁究，以减少或消除片状银粉内部的晶体缺陷，改善其微观组织，提高银粉的导电性。结果表明，热处理使塑性形变后的银粉发生回复和再结晶，晶格畸变和晶体缺陷明显减少或者部分去除。
Silver flakes made by ball milling contain large quantities of crystal defects that have negative influences on the electric conductivity of silver powders. To decrease crystal defects, ameliorate the microstructure and improve the electric conductivity, an appropriate heat treatment was established in our work. The results indicated that annealing could make milled silver flakes recover and re-crystallize, resulting in the decrease and even elimination of these lattice distortion and crystal defects.
参考文献
| [1] | 赵彬,殷有亮.银粉的形状对低温固化导电银浆导电性能的影响[J].印制电路信息,2013(09):27-29,63. |
| [2] | 银粉形貌和质量分数对油墨粘度特性和固化膜电阻的影响[J].贵金属,2012(04):60-67. |
| [3] | 肖爽,堵永国,刘其城,王宏,杨初.片状导电填料对银碳浆方阻和流变性能的影响[J].涂料工业,2013(05):1-5. |
| [4] | 朱张校.工程材料[M].北京:清华大学出版社,2001 |
| [5] | 谢明,张吉明,王松,刘满门,王塞北,陈永泰,杨有才,杨云峰,李爱坤.冷变形与热处理对Cu-Cr-Zr-Ag合金组织与性能的影响[J].贵金属,2014(01):48-51,55. |
| [6] | 谭富彬,赵玲,潘云昆,蔡云卓,黄富春.热处理对片状银粉表面性能的影响[J].贵金属,2000(04):21-24. |
| [7] | 晋勇;孙小松;薛屺.X射线衍射分析技术[M].北京:国防工业出版社,2008 |
| [8] | 郑子樵.材料科学基础[M].长沙:中南大学出版社,2013 |
| [9] | 蔡珣.材料科学与工程基础[M].上海:上海交通大学出版社,2010 |
| [10] | 李涛;杨慧.工程材料[M].北京:化学工业出版社,2013 |
| [11] | 胡赓祥;蔡珣;戎咏华.材料科学基础[M].上海:上海交通大学出版社,2006 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%