以蜜胺泡沫体为模板,采用氟化聚酰业胺制备了微孔泡沫炭.测定了其对环境中水气的吸附/脱附行为,发现:泡沫炭在空气中400℃活化1 h,可以提高其对水气的吸附能力.与活化前相比,对水气的吸附量几乎高达3倍,尽管其微孔容积仅增大了1.5倍.对环境水气中的可逆吸附率与微孔容积成线性关系,微孔容积为0.75mL/g的泡沫炭,其水气吸附率约为质最分数40%.
Microporous carbon foams were prepared from a fluorinated polyimide using melamine foam as a template. The adsorption/desorption behavior of water vapor in ambient air was examined. The activation of carbon foams at 400℃ for 1 h in air was found to be effective in increasing the adsorptivity of water vapor. The amount of water vapor adsorbed after air activation was almost 3 times as large as that before activation, although the micropore volume increase was only 1.5 times. The reversible adsorptivity for water vapor in ambient air showed a linear dependence on micropore volume with an adsorptivity of about 40% mass fraction for a micropore volume of 0.75 mL/g.
参考文献
| [1] | Kyotani T;Sonobe N;Tomita A .Formation of highly oriented graphite from polyarylonitrile by using a two-dimensional space between montmorillonite lamellae[J].Nature,1988,331:331-333. |
| [2] | Takashi Kyotani;Li-fu Tsai;Akira Tomita .Preparation of Ultrafine Carbon Tubes in Nanochannels of an Anodic Aluminum Oxide Film[J].Chemistry of Materials,1996(8):2109-2113. |
| [3] | Ryoo R;Joo S H;Jun S .Synthesis of highly ordered carbon molecular sieve via template-mediated structural transformation[J].Journal of Physical Chemistry B,1999,103:7743-7746. |
| [4] | Takashi Kyotani;Takayuki Nagai;Sanjuro Inoue .Formation of new type of porous carbon by carbonization in zeolite nanochannels[J].Chemistry of Materials,1997(2):609-615. |
| [5] | Inagaki M.Porous carbons[A].London:Elsevier,2000:124-145. |
| [6] | Inagaki M;Kang F.Pore development in carbon materials[A].北京:清华大学出版社,2006:184-225. |
| [7] | Mays T J.Active carbon fibers[A].Oxford:Elsevier Science Ltd,1999:95-118. |
| [8] | Michio Inagaki;Takahiro Morishita;Akitoshi Kuno .Carbon foams prepared from polyimide using urethane foam template[J].Carbon: An International Journal Sponsored by the American Carbon Society,2004(3):497-502. |
| [9] | Inagaki M;Ohmura M;Tanaike O .Reversible water adsorption into carbonized polyimide films in ambient atmosphere[J].Carbon,2002,40:2502-2505. |
| [10] | Ohta N;Nishi Y;Morishita T.Carbonization and pore development of carbon films derived from aromatic polyimides[J].Tanso,2008(233):174-180. |
| [11] | Ohta N;Nishi Y;Morishita T et al.Preparation of microporous carbon films from fluorinated polyimides[J].Carbon,2008,46:1350-1357. |
| [12] | Hanzawa Y.;Kaneko K. .LACK OF A PREDOMINANT ADSORPTION OF WATER VAPOR ON CARBON MESOPORES[J].Langmuir: The ACS Journal of Surfaces and Colloids,1997(22):5802-5804. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%