SOFC阴极材料(La_(0.85)Sr_(0.15))_y(Mn_(1-z)Cr_z)O

材料研究学报, 1998, 12(2): 149-153.

SOFC阴极材料(La_(0.85)Sr_(0.15))_y(Mn_(1-z)Cr_z)O_3的物理性能和化学稳定性

杨威 , 隋智通

东北大学

基金项目: 中国科学院腐蚀与防护国家重点实验室资助

关键词： SOFC , lathanum manganite. chemical stability , thermal expansion , conductivity , null

PHYSICAL PROPERTIES AND THE CHEMICAL STABILITY OF (La_0.85Sr_0.15)_y(Mn1-zCrz)O_3 AS ELECTRODE MATERIALS

YANG Wei , SUI Zhitong(Division of Metallurgical Physicochemistry of Northeastern University

Keywords： SOFC , 锰酸镧 , 化学稳定性 , 热膨胀 , 电导率

采用烧结法制备阴极材料(La0.85Sr0.15)y(Mn1z-Crz)O3(y=0.85;1;z=0.1,0.2).研究了多孔锰酸镧与致密ZrO2(8mol%Y2O3)界面的成分变化和显微形貌(La0.85Sr0.15)(Mn0.9Cr0.1)O3呈现高电子电导率、良好的热膨胀系数匹配和化学稳定性而(La0.85Sr0.15)MnO3未起到阻止界面退化的作用在1300～1500℃范围内Mn、La、Zr和Sr发生扩散,其中Mn的扩散明显

As a cathode materials the compound La0.85Sr0.15MnO3 with substitution of Cr for Mn and substoichiometry at La site was prepared by powder sintering method. The interfaces between porous La0.85Sr0.15 MnO3 layer and dense ZrO2 (Y2O3 )pellets, similar to th

参考文献

[1]

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
杨威隋智通
在百度学术搜索
杨威隋智通
在万方数据库搜索
杨威隋智通
在CNKI搜索
杨威隋智通

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网