以钠基蒙脱石为原料,采用溶胶-凝胶法制备Si溶胶柱化剂,并采用离子交换法制备硅基柱撑蒙脱石.研究了不同硅烷含量和水浴反应温度对柱撑蒙脱石的影响.X射线衍射分析表明:在硅烷含量为14 mL、水浴反应温度为50℃的条件下,制备出d(001)值为1.6114nm的硅基柱撑蒙脱石.并且研究了Si基柱撑蒙脱石催化环己醇脱水制备环己烯的反应；在Si基柱撑蒙脱石用量为环己醇质量的10％、温度为190℃、反应时间为1h时,环己烯收率可以达到71.93％.
参考文献
| [1] | Perathoner S;Vaccari A .Catalysts based on pillared interlayered clays for the selective catalytic rediction of NO[J].Clay Minerals,1997,32(01):123. |
| [2] | Macias O;Largo J;Pesquera C;Blanco C;Gonzalez F .Characterization and catalytic properties of montmorillonite pillared with aluminum/lanthanum[J].Applied Catalysis, A. General: An International Journal Devoted to Catalytic Science and Its Applications,2006(1):23-31. |
| [3] | Benito I;Del-Riego A;Martinez M et al.Toluene methylation on Al13-and GaAl12-pillared clay catalysts[J].Applied Catalysis,1999,18(1-2):175. |
| [4] | 章思规.实用精细化学品手册[M].北京:化学工业出版社,1996 |
| [5] | 郭俊胜.环己醇催化脱水制备环己烯的研究[J].化学试剂,2001(03):178-179. |
| [6] | 何节玉,廖德仲.新固体酸SO2-4-MoO3-TiO2催化制备环己烯[J].化学世界,2002(11):601-603,589. |
| [7] | 张国华,贾海宏,孙少飞,石德付.环己醇催化脱水制备环己烯[J].应用化工,2003(06):31-32. |
| [8] | 张敏,袁先友.脱铝超稳Y沸石催化环己醇脱水制备环己烯[J].精细化工,2000(05):287-289. |
| [9] | 赵曦,张广旭,王冬梅.强酸性聚苯乙烯类阳离子交换树脂催化合成环己烯[J].松辽学刊(自然科学版),2002(02):71-72. |
| [10] | 赵东源.高层间距的羟基硅铝交联蒙托土的合成与表征[J].高等学校化学学报,1992(03):295-299. |
| [11] | 赵东源;杨亚书;辛勤 等.混合金属络合物羟基镍铝交联蒙脱土的表面酸性与催化性能[J].催化学报,1993,13(03):287. |
| [12] | F. Belkhadem;A. Maldonado;B. Siebenhaar;J.-M. Clacens;M.J. Perez Zurita;A. Bengueddach;F. Figueras .Microcalorimetric measurement of the acid properties of pillared clays prepared by competitive cation exchange[J].Applied clay science,2008(1/2):28-37. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%