通过在TP347H奥氏体不锈钢中添加氮,研究了氮含量对其组织和持久性能的影响.结果表明:当氮的质量分数大于0.123%时,能有效抑制高温固溶过程中δ铁素体的析出;氮的添加明显改善了TP347H奥氏体不锈钢的室温拉伸和高温持久性能.含氮TP347H奥氏体不锈钢可作为一种新型高性能耐热材料用于超超临界火电机组.
参考文献
| [1] | LaHa K;Kyono J;Kishimoto S et al.Benificial Effect of B Segregation on Creep Cavitation in a Type 347 Austenite Stain less Steel[J].Scripta Materialia,2005,52(07):675. |
| [2] | K. Laha;J. Kyono;T. Sasaki .Improved Creep Strength and Creep Ductility of Type 347 Austenitic Stainless Steel through the Self-Healing Effect of Boron for Creep Cavitation[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2005(2):399-409. |
| [3] | 徐刚,李钧,肖学山,倪建森,朱长春,赵钧良,郑卫,王治政.硼对奥氏体耐热钢 TP347H 热加工性、组织和力学性能的影响[J].特殊钢,2008(02):23-25. |
| [4] | 张铃光,徐刚,肖学山,赵钧良,朱长春,郑卫.铈改善TP347H钢的高温持久性能研究[J].中国稀土学报,2008(06):744-747. |
| [5] | Pickering F B.High Nitrogen Steels[A].London:Inst Met,1989:17. |
| [6] | Stein G;Menzel J;Dorr H.High Nitrogen Steels[A].London:Inst Met,1989:32. |
| [7] | Gavriljuk V G;Berns H.High Nitrogen Steels[M].Berlin:springer-verlag,1999 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%