以纳米氧化锆(ZrO2)作为成核剂改性线性低密度聚乙烯(LLDPE),采用差示扫描量热仪(DSC)研究了含不同ZrO2质量分数的纳米ZrO2/LLDPE复合材料的非等温结晶行为,并分析了基于Jeziorny理论和莫志深理论的结晶动力学参数,利用Kissinger法和Takhor法计算了结晶活化能.结果表明:纳米ZrO2的加入使结晶速率变慢,阻碍了晶粒的生长;与LLDPE相比,当纳米ZrO2质量分数为10％时,复合材料的活化能降低,纳米ZrO2在结晶过程中起到异相成核的作用;而纳米ZrO2质量分数为5％时,复合材料的活化能增大,纳米ZrO2的异相成核作用不明显.
参考文献
| [1] | 孙玉梅.透明LLDPE膜专用料的研制[J].塑料工业,2005(09):59-62. |
| [2] | Kundu PP.;Biswas J.;Kim H.;Choe S. .Influence of film preparation procedures on the crystallinity, morphology and mechanical properties of LLDPE films[J].European Polymer Journal,2003(8):1585-1593. |
| [3] | Monte F.;Larsen W. .Stabilization of Tetragonal ZrO_2 in ZrO_2-SiO_2 Binary Oxides[J].Journal of the American Ceramic Society,2000(3):628-634. |
| [4] | K.J.Puolakka;S.Juutilainen;A.O.I.Krause .Combined CO_2 reforming and partial oxidation of n-heptane on noble metal zirconia catalysts[J].Catalysis Today,2006(1/4):217-221. |
| [5] | A. Barbucci;M. Viviani;P. Carpanese;D. Vladikova;Z. Stoynov .Impedance analysis of oxygen reduction in SOFC composite electrodes[J].Electrochimica Acta,2006(8/9):1641-1650. |
| [6] | 莫志深.一种研究聚合物非等温结晶动力学的方法[J].高分子学报,2008(07):656-661. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%