采用非等温DSC法对低共熔点芳胺固化剂/环氧E44体系进行了固化动力学研究,通过Kissinger、Ozawa和Crane方法获得了该体系固化动力学参数:表观活化能E=49.2 kJ/mol,固化反应级数n=0.95,频率因子A=2.60×105s-1.固化动力学方程可表示为:((dα)/(dt))=2.60×105(1-α)0.95exp(-(49200/RT)).初步确定了该体系固化工艺条件为50℃/2 h、140℃/2 h、200℃后处理2h.填料B4C加入量对该体系固化过程的DSC曲线几乎无影响.
参考文献
| [1] | 张竞,黄培.环氧树脂固化动力学研究进展[J].材料导报,2009(13):58-61,81. |
| [2] | Baller, J.;Thomassey, M.;Ziehmer, M.;Sanctuary, R. .The catalytic influence of alumina nanoparticles on epoxy curing[J].Thermochimica Acta: An International Journal Concerned with the Broader Aspects of Thermochemistry and Its Applications to Chemical Problems,2011(1/2):34-39. |
| [3] | 代晓青,曾竟成,刘钧.RFI用环氧树脂固化动力学研究[J].宇航材料工艺,2007(04):31-33. |
| [4] | 郑亚萍,宁荣昌,乔生儒.TDE-85/芳香族胺固化体系动力学研究[J].宇航材料工艺,2000(04):41-44. |
| [5] | Liu WB;Qiu QH;Wang J;Huo ZC;Sun H .Curing kinetics and properties of epoxy resin-fluorenyl diamine systems[J].Polymer: The International Journal for the Science and Technology of Polymers,2008(20):4399-4405. |
| [6] | Wang, H.;Zhu, L.;Du, Z.;Zhang, B.;Zhang, Y. .Curing behaviors and kinetics of epoxy resins with a series of biphenyl curing agents having different methylene units[J].Thermochimica Acta: An International Journal Concerned with the Broader Aspects of Thermochemistry and Its Applications to Chemical Problems,2011(1/2):18-25. |
| [7] | 赵卫娟,张佐光,孙志杰,张大兴.非等温法研究TGDDM/DDS体系固化反应动力学[J].高分子学报,2006(04):564-568. |
| [8] | 童晓梅,杨明政.非等温DSC法研究改性咪唑/环氧E44的固化反应动力学[J].陕西科技大学学报（自然科学版）,2010(05):32-36. |
| [9] | 郭清兵,陈江华,谭赟华 |
| [10] | 叶炜,王岚,李全步,黄培.低共熔点芳胺固化环氧树脂动力学研究[J].热固性树脂,2006(06):25-28. |
| [11] | 陈红宇;周润培;朱辉明.低熔点芳香胺环氧固化剂的研究—m-PDA、DDM、MOCA的三元低共熔物作为环氧固化剂的研究[J].纤维复合材料,1996(02):13-17. |
| [12] | 王斌,景宽,刘爱华,徐芳.一种低共熔点芳香胺环氧固化剂的初步研究[J].固体火箭技术,2001(02):54-57. |
| [13] | 胡玉明;吴良义.固化剂[M].北京:化学工业出版社,2004:1-143. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%