采用快速冷凝粉末包套挤压工艺制备了含 铁量分别为1.2%和3 .5%的Al-11%Si-Fe合金。 研究了这两合金在挤压和退火状态下的微观组织特征和内耗行 为 , 解释了Fe含量及其析出相、 热处理状态等对内耗的影响, 提出了该合金系在60~25 0  ℃温度范围产生内耗峰的机制。

Al-11Si-1.2Fe and Al-11Si-3.5Fe alloys were experim entally made with rapid solidification-powder extrusion technology. The interna l friction and the microstructure of the alloys under extruted and isothermal ann ealing conditions were investigated. An internal friction peak was observed in the temperature range 60~250  ℃ in the present alloys. The Q -1 peak dec reases with the increase of iron, which was found to be directly attributed to t he precipitation of FeAl2 and Al-Si-Fe intermetallics from the aluminium all o y matrix. The internal friction mechanisms of the alloy were put forward.

参考文献

[1] Zhou J;Duszczyk J;Korevaar B.Microstructural features and f inal mechanical properties of the iron-modified Al-20Si-3Cu-1Mg alloy produc t processed from atomized powder[J].Journal of Materials Science,1991(26):3041.
[2] 李月珠.快速凝固技术和材料[M].北京:冶金工业出版社,1993:22.
[3] 陈振华,张豪,刘秋林,陈刚,孙章明,杨伏良.多层喷射共沉积法制备6066铝合金/SiC颗粒复合材料[J].中国有色金属学报,1996(04):83-86.
[4] 郭鸿镇,姚泽坤,花田修治,吉见享袺.快速凝固Nb3Al-Nb固溶体再相合金的组织与性能[J].中国有色金属学报,1998(03):472-476.
[5] 袁晓光;徐达鸣 .喷射沉积Al-Si-Fe-Cu -Mg合金组织与力学性能[J].金属学报,1997,33(03):248-252.
[6] Fabietti L M;Sekhar J A .Planar to equiaxed transition in the presenc e of an external wetting surface[J].Metallurgical and Materials Transactions,1992,23:3361.
[7] Nowick A S;Berry B S.Anelastic Relaxation in Crystalline solids[M].New York:Academic Press,1972:435.
[8] 冯端;王业宁;丘第荣.Metal Physics B(金属物理B)[M].北京:科学出版社,1975:557.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%