采用电火花沉积工艺,用WC陶瓷硬质合金在铸钢轧辊表面制备了一层合金涂层。采用X射线衍射仪、扫描电镜、显微硬度计等对沉积层的相结构、显微组织、显微硬度及耐磨性能进行了分析。结果表明：沉积层主要由Co3W3C、Fe3W3C、W2C、Si2W等相组成;沉积层与基体呈冶金结合,细小的硬质相弥散分布于沉积层中;沉积层的平均硬度为1915 HV0.3,约是基体硬度（352 HV0.3）的5.4倍;其室温耐磨性能比基体提高了2.1倍,高温耐磨性能比基体提高了1.9倍。室温下沉积层的主要磨损机理为磨粒磨损;高温下沉积层的主要磨损机理为粘着磨损、氧化磨损和疲劳磨损。
参考文献
| [1] | Jian-sheng Wang,Hui-min Meng,Hong-ying Yu,Zi-shuan Fan,Dong-bai Sun.Characterization and wear behavior of WC-0.8Co coating on cast steel rolls by electro-spark deposition[J].矿物冶金与材料学报,2009(06):707-713. |
| [2] | 张鲲;何业东;王德仁 .电火花沉积MCrAIY涂层及其高温氧化行为[J].材料热处理学报,2008,29(04):143-147. |
| [3] | WANG Jiansheng,MENG Huimin,YU Hongying,FAN Zishuan,SUN Dongbai.Wear characteristics of spheroidal graphite roll WC-8Co coating produced by electro-spark deposition[J].稀有金属(英文版),2010(02):174-179. |
| [4] | 罗成,熊翔,董仕节,罗平.点焊电极表面电火花沉积TiB_2涂层的特征[J].材料热处理学报,2009(06):178-182. |
| [5] | WANG Jiansheng,MENG Huimin,YU Hongying,FAN Zishuan,SUN Dongbai.Wear characteristics of spheroidal graphite roll WC-8Co coating produced by electro-spark deposition[J].稀有金属(英文版),2010(02):174-179. |
| [6] | Ribalko AV.;Sahin O. .The use of bipolar current pulses in electrospark alloying of metal surfaces[J].Surface & Coatings Technology,2003(2/3):129-135. |
| [7] | 罗成,董仕节,熊翔.电火花振动沉积TiC功能涂层的显微组织与性能[J].材料热处理学报,2008(02):123-127. |
| [8] | 邵荷生;曲敬信;许小棣.摩擦与磨损[M].北京:煤炭工业出版社,1992 |
| [9] | 王建升,高玉新,张瑞珠.铸钢材料电火花表面沉积WC-4Co涂层的组织与性能[J].材料热处理学报,2010(12):123-128. |
| [10] | 乔生儒,韩栋,李玫.钢铁表面电火花淬火组织超细化及机理[J].机械工程材料,2004(08):7-9. |
| [11] | Wang R J;Qian Y Y;Liu J .Structural and interfacia! analysis of WC92-Co8 coating deposited on titanium alloy by electrospark deposition[J].Applied Surface Science,2004,228(04):405-409. |
| [12] | 梁秀兵,程江波,刘燕,白金元,徐滨士.铁基非晶纳米晶涂层的耐磨性研究[J].装甲兵工程学院学报,2009(05):77-81. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%