采用新型扭动微动试验机在法向载荷为50、80和110 N及角位移幅值为0.3°～10°的条件下进行TA2和TC4合金与ZrO2对磨球的扭动微动试验.在摩擦动力学行为研究的基础上,结合磨痕形貌微观分析,考察TA2和TC4合金的扭动微动磨损特性.结果表明:可用摩擦扭矩—角位移曲线和摩擦扭矩时变曲线表征合金的扭动微动行为,获得了TA2和TC4合金的扭动微动运行工况微动图,TA2合金的混合区较TC4合金的宽.摩擦扭矩随法向载荷和角位移幅值的增加而增加,在相同试验条件下,TA2合金的摩擦扭矩始终大于TC4合金的.在部分滑移区,损伤轻微；在混合区和滑移区,损伤加剧,扭动微动摩擦磨损机制主要为磨粒磨损、氧化磨损和剥落.
参考文献
| [1] | 周仲荣;朱旻昊.复合微动磨损[M].上海:上海交通大学出版社,2004:1-235. |
| [2] | B. J. Briscoe;A. Chateauminois;T. C. Lindley;D. Parsonage .Fretting wear behaviour of polymethylmethacrylate under linear motions and torsional contact conditions[J].Tribology International,1998(11):701-711. |
| [3] | B. J. Briscoe;A. Chateauminois;T. C. Lindley;D. Parsonage .Contact damage of poly(methylmethacrylate) during complex microdisplacements[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2000(1/2):27-39. |
| [4] | B. J. Briscoe;A. Chateauminois .Measurements of friction-induced surface strains in a steel/polymer contact[J].Tribology International,2002(4):245-254. |
| [5] | Chateauminois A.;Briscoe BJ. .Nano-rheological properties of polymeric third bodies generated within fretting contacts[J].Surface & Coatings Technology,2003(0):435-443. |
| [6] | 蔡振兵 .扭动微动磨损机理研究[D].西南交通大学,2009. |
| [7] | 俞佳 .超高分子量聚乙烯的扭动微动磨损机理研究[D].成都:西南交通大学,2008. |
| [8] | 林修洲 .钛合金扭动微动腐蚀行为研究[D].西南交通大学,2010. |
| [9] | 蔡振兵,朱旻昊,张强,何莉萍,林修洲.钢-钢接触的扭动微动磨损氧化行为研究[J].西安交通大学学报,2009(09):86-90. |
| [10] | 卫中山,王珉,左敦稳,李亮.钛合金的微动疲劳及其防护[J].材料科学与工程学报,2003(02):293-297. |
| [11] | 刘莹,曲周德,王本贤.钛合金TC4的研究开发与应用[J].兵器材料科学与工程,2005(01):47-50. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%