以磷石膏为原料,利用蒸压法制备半水硫酸钙晶须.采用均匀设计实验的基础上,进一步考察了料浆固液比、反应时间、蒸压压力对产品长径比的影响,并借助透射偏光显微镜、X射线衍射仪(XRD)等仪器对产品进行表征.结果表明,最佳反应条件:料浆固液比0.15 g· mL-1、反应时间0.5h、蒸压的压力0.3 MPa,在此条件下制备出了长径比99.07、晶须直径约1μm、纯度高、结晶良好的晶须产品.并从微观形貌、晶体结构、物相分析三个方面阐明了半水硫酸钙晶须生长规律.本研究对磷石膏的高值化利用具有指导意义.
参考文献
| [1] | 韩青;罗康碧;李沪萍;孔霞;苏毅.磷石膏开发利用现状[J].化工科技,2012(1):53-58. |
| [2] | 杨兆娟;向兰.磷石膏综合利用现状评述[J].无机盐工业,2007(1):8-10. |
| [3] | 徐爱叶;李沪萍;罗康碧.磷石膏中杂质及除杂方法研究综述[J].化工科技,2010(6):59-64. |
| [4] | 钱文敏;唐芬;许中俊;王秋姮.云南磷石膏综合利用现状及次生环境问题[J].环境科学导刊,2015(1):58-60. |
| [5] | 黄哲元;董发勤;张伟.硫酸钙晶须的制备进展[J].无机盐工业,2009(8):6-8. |
| [6] | 张华伟;陈继涛;梁鹏;王力.硫酸钙晶须制备机理及技术研究进展[J].材料导报,2011(11):46-50,75. |
| [7] | 秦军;谢占金;于杰;金翠霞;解田;杨丽萍.磷石膏制备硫酸钙晶须的初步研究[J].无机盐工业,2010(10):50-53. |
| [8] | Yongqian Wang;Yinchang Li;Ao Yuan;Bo Yuan;Xinrong Lei;Qun Ma;Jun Han;Junxia Wang;Jieyu Chen.Preparation of calcium sulfate whiskers by carbide slag through hydrothermal method[J].Crystal Research and Technology: Journal of Experimental and Industrial Crystallography,201410(10):800-807. |
| [9] | Xiao Wang;Liushuan Yang;Xinfeng Zhu;Jiakuan Yang.Preparation of calcium sulfate whiskers from FGD gypsum via hydrothermal crystallization in the H2SO4-NaCl-H2O system[J].颗粒学报（英文版）,2014(6):42-48. |
| [10] | 袁致涛;王宇斌;韩跃新;李丽匣.半水硫酸钙晶须稳定化研究[J].无机化学学报,2008(7):1062-1067. |
| [11] | 韩跃新;王宇斌;袁致涛;印万忠.半水硫酸钙晶须水化过程[J].东北大学学报（自然科学版）,2008(10):1490-1493. |
| [12] | Boisvert JP.;Foissy A.;Persello J.;Mutin JC.;Domenech M..Hydration of calcium sulfate hemihydrate (CaSO4 center dot 1/2H2O) into gypsum (CaSO4 center dot 2H(2)O). The influence of the sodium poly(acrylate)/surface interaction and molecular weight[J].Journal of Crystal Growth,20004(4):579-591. |
| [13] | Pradip K. Mandal;Tanuj K. Mandal.Anion water in gypsum (CaSO_4 centre dot 2 H_2O) and hemihydrate (CaSO_4 centre dot 1/2 H_2O)[J].Cement and Concrete Research,20022(2):313-316. |
| [14] | Follner S.;Wolter A.;Preusser A.;Indris S.;Silber C.;Follner H..The setting behaviour of alpha- and beta-CaSO4 center dot 0,5 H2O as a function of crystal structure and morphology[J].Crystal Research and Technology: Journal of Experimental and Industrial Crystallography,200210(10):1075-1087. |
| [15] | Rashad MM.;Baioumy HM.;Abdel-Aal EA..Structural and spectral studies on gypsum crystals under simulated conditions of phosphoric acid production with and without organic and inorganic additives[J].Crystal Research and Technology: Journal of Experimental and Industrial Crystallography,20036(6):433-439. |
| [16] | 杨娜;肖汉宁;郭文明.添加剂辅助水热法制备硫酸钙晶须及生长机理研究[J].硅酸盐学报,2014(4):539-544. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%