采用真空热压烧结技术制备了多种MoSi2基复合材料,研究了强韧相对复合材料组织与性能的影响,并对其复合强韧化机理进行了探讨.结果表明:强韧相的加入均能不同程度地提高MoSi2的强韧性,其强韧化效果取决于强韧相的数量、种类和含量,数量以两相为宜;其中两相强韧化5%SiC+5%Nb/MoSi2 复合材料的性能较优,其显微硬度、断裂韧度、抗弯强度分别为12.86 GPa,11.42 MPa·m<'1/2>,470 MPa,比热压烧结纯MoSi2分别提高了31.22%,223.5%和70.9%;多元MoSi2基复合材料的强韧化机理表现为各强韧相的协同作用,其效果取决于各强韧相之间的匹配性.
参考文献
| [1] | M. Zakeri;R. Yazdani-Rad;M.H. Enayati .Synthesis of MoSi_2-Al_2O_3 nanocomposite by mechanical alloying[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2006(1/2):185-188. |
| [2] | J. Meng;J. Lu;J. Wang .Preparation and properties of MoSi_2 composites reinforced by TiC, TiCN, and TiB_2[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):277-284. |
| [3] | Hebsur MG .Development and characterization of SiC sub (f) /MoSi sub 2 -Si sub 3 N sub 4(p) hybrid composites[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1999(1/2):24-37. |
| [4] | 吴海飞,徐金富,费有静,陈胜,张学彬,叶以富.第二相对MoSi2基复合材料组织与性能的影响[J].材料热处理学报,2007(z1):331-334. |
| [5] | 徐金富,陈胜,吴海飞,文小浩.多相强韧化MoSi2基复合材料的制备及性能[J].机械工程材料,2008(12):72-75. |
| [6] | 徐金富,费有静,张学彬,张亚非,吴海飞.纳米ZrO2颗粒增强MoSi2基复合材料的显微组织和力学性能[J].金属热处理,2007(06):33-36. |
| [7] | 桂尤国,徐金富,叶以富.MoSi2基复合材料的室温韧性研究[J].粉末冶金工业,2006(02):5-8. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%