以硅藻土为主要原料,采用固相烧结法,制备了硅藻土基微孔陶瓷,探讨了粉体粒度对其比表面积、烧结样品的孔径及其分布、孔隙率等性能的影响.结合SEM、BET、压汞仪等手段对样品进行了表征.结果表明:在d50=3.57～1.17 μm间,随粉体粒度的减小,粉体比表面积上升,烧结样品的平均孔径及孔隙率下降,其后孔径分布变宽并出现团聚;d50=1.17 μm时,粉体比表面积48.59 m2/g,烧结样品平均孔径157.8 nm,孔隙率39.3%;对孔雀石绿溶液的脱色研究表明,粉体粒度减小,多孔陶瓷的脱色能力增强,反应420 min,d50=1.17 μm粉体烧结样品的脱色率达90.8%.
参考文献
| [1] | Wang HT.;Chen FL.;Meng GY.;Sorensen OT.;Liu XQ. .Kinetics and mechanism of a sintering process for macroporous alumina ceramics by extrusion[J].Journal of the American Ceramic Society,1998(3):781-784. |
| [2] | Ya-Fei Liu;Xing-Qin Liu;Shan-Wen Tao;Guang-Yao Meng;O. Toff Sorensen .Kinetics of the reactive sintering of kaolinite-aluminum hydroxide extrudate[J].Ceramics International,2002(5):479-486. |
| [3] | Xuebin Zhang;Xingqin Liu;Guangyao Meng .Sintering Kinetics of Porous Ceramics from Natural Diatomite[J].Journal of the American Ceramic Society,2005(7):1826-1830. |
| [4] | Y.al-Degs;M.A.M.Khraisheh;M.F.tutunji .Sorption of lead ions on diatomite and manganese oxides modified diatomite[J].Water research: A journal of the international water association,2001(15):3724-3728. |
| [5] | 孙宏伟;钟顺和;张鎏.硅藻土微孔陶瓷膜管的制备与性能[J].硅酸盐通报,1997(05):51-53. |
| [6] | Vasconcelos P V;Labrincha J A;Ferreira J M F .Porosity Development of Diatomite Layers Processed by Tape Casting[J].Ceramics International,1998,24:447-454. |
| [7] | 李世普.特种陶瓷工艺学[M].武汉:武汉工业大学出版社,1990:1. |
| [8] | 高如琴.刚玉瓷指痕缺陷的研究[J].中国陶瓷工业,2002(05):29-32. |
| [9] | 郝保红;郑水林;毛钜凡 .粉石英细磨过程中的团聚现象[J].粉体技术,1997,4(03):6-11. |
| [10] | 王连星;宁青菊;姚治才.多孔陶瓷材料[J].硅酸盐通报,1998(01):41-45. |
| [11] | 周健儿,张小珍,李家科,胡学兵.透气过滤用堇青石蜂窝陶瓷材料的研究[J].中国陶瓷,2006(02):3-7. |
| [12] | 吴道政;周竹发 .微米级多孔Al2O3的研制[J].江苏陶瓷,1999,15(03):23-26. |
| [13] | 黄文强;李晨曦.吸附分离材料[M].北京:化学工业出版社,2005:91. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%