采用固相反应法制备了K_(0.44)Na_(0.52)Li_(0.04)Nb_(0.86)Ta_(0.10)Sb_(0.04)O_3+x mol %K_4CuNb_8O_(23)(0≤x≤2)(简称LF4-KCN)无铅压电陶瓷,使用XRD、SEM、 Agilent 4294A精密阻抗分析仪等对该体系的相组成、显微结构、压电及介电等性能进行表征.XRD分析表明,随着KCN含量的增加,室温时样品由四方相向正交相转变,且当x≥1时,出现K_6Li_4Nb_(10)O_(30)杂相.SEM分析表明,掺入KCN后,样品晶粒尺寸减小,晶粒轮廓清晰.随着KCN含量的增加,在100 ℃附近的介电常数温度曲线上出现第二介电常数极大值,即正交→四方铁电相变温度T_(O-T),同时居里温度TC向低温方向移动.KCN掺杂量对LF4的电性能有很大影响,表现为"硬性"掺杂,其压电常数d_(33),平面机电耦合系数k_p,1kHz频率下的介电损耗tanδ和介电常数ε_r均随着 KCN含量的增加而降低,而机械品质因素Q_m整体提高,样品的密度也显著增大.

The K_(0.44)Na_(0.52)Li_(0.04)Nb_(0.86)Ta_(0.10)Sb_(0.04)O_3+x mol%K_4CuNb_8O_(23)(0≤x≤2)(abbreviated as LF4-KCN) lead-free piezoelectric ceramics were fabricated by solid state reaction. The phase, microstructure, electric properties of the samples were characterized by XRD, SEM and Agilent 4294A impedance analyzer. XRD result shows that the phase of the sample transforms from tetragonal into orthorhombic with the increasing of KCN content. When x≥1, the trace amount of second phase K_6Li_4Nb_(10)O_(30) can be detected. SEM shows that the grain size of those materials decreases as the KCN content increasing, and the figure of the grain becomes clearly. There is another dielectric constant maximum value around 100 ℃, which is the phase transition from orthorhombic to tetragonal (T_(O-T)), while the curie temperature (TC) shifts to higher temperature. The KCN-doping has great influence on the electrical properties, the ceramic becomes "hardened", the piezoelectric constant (d_(33)), electromechanical planar coupling coefficients(kp), the dielectric constant(ε_r) and dielectric loss(tanδ) at 1 kHz decrease as the KCN content increasing. The mechanical quality factor (Q_m) and the density increases significantly.

参考文献

[1] 肖定全,万征.环境协调型压电铁电陶瓷[J].压电与声光,1999(05):363-366.
[2] Cross E .Lead-free at Last[J].NATURE,2004,432(04):24.
[3] Guo, YP;Kakimoto, K;Ohsato, H .Ferroelectric-relaxor behavior of (Na0.5K0.5)NbO3-based ceramics[J].The journal of physics and chemistry of solids,2004(11):1831-1835.
[4] Matsubara M;Yamaguchi T;Kikuta K et al.Sinterability and Piezoelectric Properties of (K,Na)NbO_3 Ceramics with Novel Sintering Aid[J].Japanese Journal of Applied Physics,2004,43(10):7159-7163.
[5] Matsubara M;Yamaguchi T;Kikuta K et al.Synthesis and Characterization of (K_(0.5)Na_(0 5.O_3 Piezoelectric Ceramics Sintered with Sintering[J].Japanese Journal of Applied Physics,2005,44(9A):6618-6623.
[6] 胡晓萍,刘晓东,曾敏,李龙珠,江向平.铜掺杂对(Na0.5K0.5)NbO3无铅压电陶瓷性能的影响[J].陶瓷学报,2005(04):235-238.
[7] Park S H;Ahn C W;Nahm S et al.Microstructure and Piezoelectric Properties of ZnO-added K_(0.5)Na_(0 5)NbO_3 Ceramics[J].Japanese Journal of Applied Physics,2004,43(8B):1072-1074.
[8] Saito Y;Takao H;Tani T et al.Lead-free Piezoceramics[J].NATURE,2004,432(7013):84-87.
[9] 江向平,胡晓萍,江福兰,刘晓冬,殷庆瑞.Li改性铌钽酸钾钠无铅压电陶瓷的研究[J].无机材料学报,2007(03):465-468.
[10] 唐福生 .(K<,0.5>Na<,0.5>)NbO<,3>-LiNbO<,3>无铅压电陶瓷的制备及性能研究[D].西北工业大学,2007.
[11] 刘梅冬;许毓春.压电铁电材料与器件[M].武汉:华中理工大学出版社,1992:46-47.
[12] 陈建华,屈绍波,高坤华,裴志斌,朱林户.锰掺杂对(Na0.5Bi0.5)TiO3-BaTiO3-(K0.5Bi0.5)TiO3陶瓷介电和压电性能的影响[J].稀有金属材料与工程,2006(11):1704-1707.
[13] 关振铎;张中太;焦金生.无机材料物理性能[M].北京:清华大学出版社,2004:327-329.
[14] Guo Y;Kakimoto K;Ohsato H .Phase Transitional Behavior and Piezoelectric Properties of (Na_(0.5)K_(0 5)Nb_3-LiNbO_3 Ceramics[J].Applied Physics Letters,2004,85(18):4121-4123.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%