Microstructure and mechanical properties of X80 pipeline steels in different cooling schedules

金属学报(英文版), 2010, (3): 171-175.

^1, , ^2, , ^3,

1.State Key Laboratory of Rolling Technology and Automation, Northeastern University, Shenyang 110819, China

2.State Key Laboratory of Rolling Technology and Automation, Northeastern University, Shenyang 110819, China

3.State Key Laboratory of Rolling Technology and Automation, Northeastern University, Shenyang 110819, China

关键词： X80级管线钢 , 冷却降温 , 时间表 , 力学性能 , 显微组织 , 落锤撕裂试验 , X80管线钢 , 微观结构

Microstructure and mechanical properties of X80 pipeline steels in different cooling schedules

Min ZHOU ^1, , Linxiu DU ^2, , Xianghua LIU ^3,

1.State Key Laboratory of Rolling Technology and Automation, Northeastern University, Shenyang 110819, China

2.State Key Laboratory of Rolling Technology and Automation, Northeastern University, Shenyang 110819, China

3.State Key Laboratory of Rolling Technology and Automation, Northeastern University, Shenyang 110819, China

Keywords： Microstructure , Mechanical properties , Cooling schedule , Relaxation ,

The microstructures and mechanical properties of three X80 pipeline steel plates were investigated in this study.The plates were hot rolled by two stages, and cooled by three different cooling schedules to obtain different microstructures and mechanical properties.Transmission electron microscope（TEM） was used to observe the microstructure.The results indicated that the amount of polygonal ferrite（PF） and quasi-polygonal ferrite（QPF） decreased with decreasing of the finish cooling temperature（FCT）, while the amount and size of M-A islands were larger.Relaxation promoted the Charpy V-notch（CVN） impact toughness at-20℃, but not the drop weight tear testing（DWTT） property at-15℃, and decreased the strength of the steel.

参考文献

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Microstructure and mechanical properties of X80 pipeline steels in different cooling schedules

参考文献